1
المؤلفون: Bulidon, Nicolas, Pélissier, Krystel, Boissy, Clément, Mendibide, Christophe, Maillot, Valérie, Bourbon, Xavier, Crusset, Didier
المصدر: Materials and corrosion - Werkstoffe und Korrosion. 74(11-12):1765-1776
مصطلحات موضوعية: Alkalinity, Aluminum corrosion, Cements, Corrosion rate, Corrosive effects, Electrochemical corrosion, Hydrogen storage, Radioactive wastes, Alkaline environment, Aluminum can, Cement encapsulation, Cement-based matrices, Corrosion products, Deep geological disposal, Electrochemical measurements, Hydrogen-evolution, Long-lived radioactive wastes, Nuclear waste disposal, Hydrogen production
وصف الملف: print
-
2دورية أكاديمية
المؤلفون: Loder, Bernd, Bhosale, Saurabh, Eichinger, Matthias, Mori, Gregor, Rokosz, Krzysztof, Fournier, Cyriane, Reveillere, Arnaud, Bulidon, Nicolas, Moli-Sanchez, Laura, Mendibide, Christophe
المصدر: In International Journal of Hydrogen Energy 22 February 2024 56:232-241
-
3
المؤلفون: Mendibide, Christophe, Vucko, Flavien, Martinez, M, Joshi, GR, Kittel, J
المصدر: International journal of hydrogen energy. 52:1019
مصطلحات موضوعية: Fracture toughness, Hydrogen induced cracking, Hydrogen permeation, Hydrogen transport, Pipeline, Slow strain rate test, Cracks, Digital storage, Ductile fracture, Fossil fuels, Fracture testing, Hydrogen, Hydrogen embrittlement, Natural gas, Steel pipe, Strain rate, 'Dry' [, Environmental conditions, Green energy, Service behaviors, Slow strain rate tests, Steel grades, X65 pipe-line steel, Pipelines
وصف الملف: electronic
-
4
المؤلفون: Bulidon, Nicolas, Deydier, Valerie, Bumbieler, Frederic, Duret-Thual, Claude, Mendibide, Christophe, Crusset, Didier
المصدر: Materials and corrosion - Werkstoffe und Korrosion. (1-2):154-165
مصطلحات موضوعية: geological repository, radioactive waste, stress corrosion cracking, Cements, Cracks, Geological repositories, Grouting, Mortar, Radioactive waste disposal, Radioactive waste storage, Radioactive wastes, Radioactivity, Residual stresses, Steel corrosion, Strain rate, Tensile testing, Crack initiation and propagation, Deep geological repository, Electrochemical measurements, High level radioactive waste repositories, High level radioactive wastes, Long-term immersions, Slow strain rate tensile test, Stress corrosion cracking susceptibility
وصف الملف: print
-
5
المؤلفون: Mendibide, Christophe, Dusquesnes, Vincent, Deydier, Valerie, Bourbon, Xavier, Crusset, Didier
المصدر: Materials and corrosion - Werkstoffe und Korrosion. 72(1-2):383-395
مصطلحات موضوعية: aluminum, cement encapsulation, hydrogen evolution, nuclear waste management, resaturation, Aluminum corrosion, Cement industry, Cements, Corrosion rate, Corrosion resistance, Corrosion resistant alloys, Corrosive effects, Hydrogen production, Radioactive waste disposal, Radioactive wastes, Radioactivity, Alkaline environment, Cement-based matrices, Corrosion behavior, Deep geological disposal, Disposal facilities, Evolution of hydrogens, Nuclear waste dis-posal, Surface disposal facility, Aluminum alloys
وصف الملف: print
-
6
المؤلفون: Mendibide, Christophe, Dessolin, Carole
المصدر: Corrosion. 79(2):174-192
مصطلحات موضوعية: Cracking, Duplex stainless steel, H2S, Selective dissolution, Cold rolling, Dissolution, Metal cladding, Stainless steel, Steel corrosion, Steel sheet, Steel testing, Applied stress, Cold-rolled, Condition, Crystallographic orientations, Electrochemical monitoring, Electron backscattered diffraction analysis, Passive films, Test condition, Types of corrosions, Sodium chloride
وصف الملف: print
-
7دورية أكاديمية
المؤلفون: Deffo Ayagou, Martien Duvall, Joshi, Gaurav R., Mai Tran, Thi Tuyet, Tribollet, Bernard, Sutter, Eliane, Mendibide, Christophe, Duret-Thual, Claude, Kittel, Jean *
المصدر: In Corrosion Science March 2020 164
-
8مؤتمر
المؤلفون: Mendibide, Christophe
المساهمون: Aperam R&D, French Corrosion Institute
المصدر: CORROSION 2018.
-
9دورية أكاديمية
المؤلفون: Deffo Ayagou, Martien Duvall, Mai Tran, Thi Tuyet, Tribollet, Bernard, Kittel, Jean, Sutter, Eliane, Ferrando, Nicolas, Mendibide, Christophe, Duret-Thual, Claude
المصدر: In Electrochimica Acta 20 August 2018 282:775-783
-
10
المؤلفون: Ayagou, Martien, Joshi, G. R., Tran, T. T. M., Sutter, E., Tribollet, B., Mendibide, Christophe, Duret-Thual, Claude, Ferrando, N., Kittel, J.
المصدر: Corrosion. 75(4):389-397
مصطلحات موضوعية: Hydrogen permeation, Hydrogen sulfide, Hydrogen-induced cracking, Sulfide stress cracking, Contamination, Corrosion rate, Gas industry, Hydrogen embrittlement, Materials testing, Partial pressure, Permeation, Solution mining, Sulfur compounds, Electrochemical data, Engineering standards, Hydrogen induced cracking, Oxygen contamination, Surface characterization, Weight loss measurements, Iron
وصف الملف: print