Durability of Ultra-Thin Silver Films and Silver—Gold Alloy Films under UV Irradiation.
| العنوان: | Durability of Ultra-Thin Silver Films and Silver—Gold Alloy Films under UV Irradiation. |
|---|---|
| المؤلفون: | Ming Zhou, Yuan Cai, Yao-Peng Li, Ding-Quan Liu |
| المصدر: | Chinese Physics Letters; Oct2016, Vol. 33 Issue 10, p1-1, 1p |
| مصطلحات موضوعية: | SILVER-gold alloys, METAL coating, SILVER, DURABILITY, ULTRAVIOLET radiation, THIN films, EVAPORATION (Chemistry) |
| مستخلص: | Silver films (Ag) and silver—gold films (Ag—Au) with thickness ∼15 nm are coated on Bk7 glasses through thermal evaporation. After doping gold of 5.2%, the grain size of the Ag film reduces from 13.6 nm to 9.1 nm, also the surface roughness decreases from 1.45nm to 0.94nm. A UV lamp is used as the irradiation light source to accelerate the corrosion process in the atmosphere. After 17h irradiation, the pure silver film surface turns dark, and the transmittances reduce from 350 nm to 500 nm, while the Ag—Au film degrades much less, almost negligibly after UV radiation. Additional x-ray photoelectron spectroscopy and atomic force micrographs data are provided to show atomic content of films and their surface morphologies. It is suggested that small grain size and high packing density of alloy film prevent reaction of silver with oxygen in the atmosphere, which leads to high stability of the Ag—Au film. [ABSTRACT FROM AUTHOR] |
| Copyright of Chinese Physics Letters is the property of IOP Publishing and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) | |
| قاعدة البيانات: | Complementary Index |
Full Text Finder كن أول من يترك تعليقا!