Bonding of Fused Quartz with an Aromatic Silane Compound and Acidic Functional Monomers with a Tri-n-butylborane Initiated Resin.
| العنوان: | Bonding of Fused Quartz with an Aromatic Silane Compound and Acidic Functional Monomers with a Tri-n-butylborane Initiated Resin. |
|---|---|
| المؤلفون: | Tomoyo Okazaki, Hiroyasu Koizumi, Haruto Hiraba, Akihisa Kodaira, Takayuki Yoneyama, Hideo Matsumura |
| المصدر: | Journal of Adhesive Dentistry; 2020, Vol. 22 Issue 6, p615-624, 10p |
| مصطلحات موضوعية: | FUSED silica, SILANE compounds, MONOMERS, AROMATIC compounds, DENTAL adhesives, BOND strengths |
| مستخلص: | Purpose: This study evaluated the effect of an aromatic silane compound and acidic functional monomer on the bond strength of fused quartz. Materials and Methods: A total of 264 disk specimens were fabricated from fused quartz for shear bond testing. Two silane compounds were used: 3-(trimethoxysilyl)propyl methacrylate (3-TMSPMA) and 3-(4-methacryloyloxyphenyl)propyltrimethoxysilane (3-MPPTS). As acidic functional monomers, 4-methacryloyloxyethyl trimellitate (4-MET) and 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) were used. The disks were primed with one of each silane compound with or without the acidic functional monomer of the same molarity. The specimens were bonded with a tri-n-butylborane (TBB) initiated luting material. The shear bond strength was determined before and after 10,000 thermocycles. Bond strength was statistically evaluated with Kruskal-Wallis, Mann-Whitney U-, and Steel-Dwass tests. To test dye penetration, the specimens were immersed in 0.5 wt% fuchsin solution for 24 h after priming with each condition, bonding, and 10,000 thermocycles. The dye penetration area was determined by observing the backside of the bonded specimen with an optical microscope. The relationship between the shear bond strength and dye penetration ratio was analyzed with Spearman's rank correlation test. Results: The highest post-thermocycling bond strengths in the 1 mol% and 2 mol% groups were 3-TMSPMA + 10-MDP and 3-MPPTS + 10-MDP. Spearman's rank correlation coefficient between shear bond strength and dye penetration area was γ = -0.7519, indicating a strong negative correlation. Conclusion: The surface treatments of 3-TMSPMA and 3-MPPTS combined with 10-MDP yielded higher bond strength after 10,000 thermocycles than those combined with 4-MET, despite the similarity in molarity. The shear bond strength was negatively correlated with the dye penetration area. [ABSTRACT FROM AUTHOR] |
| Copyright of Journal of Adhesive Dentistry is the property of Quintessence Publishing Company Inc. and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) | |