Defect structures in (001) zincblende GaN/3C-SiC nucleation layers.
| العنوان: | Defect structures in (001) zincblende GaN/3C-SiC nucleation layers. |
|---|---|
| المؤلفون: | Vacek, Petr, Frentrup, Martin, Lee, Lok Yi, Massabuau, Fabien C.-P., Kappers, Menno J., Wallis, David J., Gröger, Roman, Oliver, Rachel A. |
| المصدر: | Journal of Applied Physics; 4/21/2021, Vol. 129 Issue 15, p1-10, 10p |
| مصطلحات موضوعية: | SCANNING transmission electron microscopy, DISLOCATION loops, NUCLEATION, DISLOCATIONS in metals, DISLOCATION nucleation, GALLIUM nitride films |
| مستخلص: | The defect structure of zincblende GaN nucleation layers grown by metalorganic vapor-phase epitaxy on 3C-SiC/Si (001) was investigated by high-resolution scanning transmission electron microscopy. Perfect dislocations, partial dislocations, and stacking faults are present in the layers. Perfect dislocations are identified as 60° mixed-type and act as misfit dislocations to relieve the compressive lattice mismatch strain in GaN. Stacking faults are mainly bounded by 30° Shockley partial dislocations and rarely by Lomer–Cottrell partial dislocations, both of which are able to relieve the compressive lattice mismatch strain in the layer. We propose that the stacking faults and their partial dislocations originate from the dissociation of perfect dislocations present in the zincblende GaN layer and by direct nucleation of partial dislocations loops from the surface. These are the two main mechanisms that lead to the final defect structure of the zincblende GaN nucleation layers. [ABSTRACT FROM AUTHOR] |
| Copyright of Journal of Applied Physics is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) | |
| قاعدة البيانات: | Complementary Index |
Find this article in full text from Scitation. كن أول من يترك تعليقا!