Comparison of Fracture Resistance and Failure Mode in Digitally Milled Restorations with Rapid Layering by Indirect Composite Resin: An In Vitro Study.
العنوان: | Comparison of Fracture Resistance and Failure Mode in Digitally Milled Restorations with Rapid Layering by Indirect Composite Resin: An In Vitro Study. |
---|---|
المؤلفون: | Ghodsi, Safoura, Zeighami, Somayeh, Etemad, Mahta |
المصدر: | International Journal of Oral & Maxillofacial Implants; Sep/Oct2021, Vol. 36 Issue 5, p924-928, 5p, 1 Color Photograph, 1 Diagram, 2 Charts |
مصطلحات موضوعية: | DENTAL implants, POLYETHER ether ketone, COMPUTER-aided design, IN vitro studies |
مستخلص: | Purpose: To evaluate the fracture resistance and failure mode of implant crowns made by polyether ether ketone (PEEK), zirconia, and chromium-cobalt frames, veneered by milled composite resin. Materials and Methods: Thirty-six implant analogs were mounted in acrylic blocks, and solid abutments were secured (n = 12). Single-unit frameworks were milled from PEEK, zirconia, or chromium-cobalt, and cemented to indirect composite veneers fabricated by the rapid layering technique. After thermal cycling, the fracture resistance test was performed at a speed of 0.5 mm/min, and the results were statistically analyzed by one-way analysis of variance (ANOVA) and Tukey post hoc test (P < .05). The failure mode was evaluated by a stereomicroscope ('10). Veneer failure without damage to other components was considered desirable (repairable). Results: The mean fracture resistances of PEEK, zirconia, and chromium-cobalt specimens were 2,037.24, 2,567.05, and 2,032.10 N, respectively. The Tukey post hoc test showed no significant difference between the PEEK and chromium-cobalt groups (P = .99); however, the difference was significant between zirconia and PEEK or chromium-cobalt specimens (P = .001). Failure mode was desirable in all chromium-cobalt (12 specimens), 9 zirconia, and 7 PEEK-based specimens. Conclusion: Zirconia-composite implant crowns had significantly higher fracture resistance. Given the range of maximum occlusal forces, all the specimens had clinically acceptable results. The failure mode was more desirable in chromium-cobalt, followed by zirconia-based crowns. [ABSTRACT FROM AUTHOR] |
Copyright of International Journal of Oral & Maxillofacial Implants is the property of Quintessence Publishing Company Inc. and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) | |