Dynamic mechanical behaviors of epoxy resin/hollow polymeric microsphere composite foams under forced non-resonance and forced resonance.
العنوان: | Dynamic mechanical behaviors of epoxy resin/hollow polymeric microsphere composite foams under forced non-resonance and forced resonance. |
---|---|
المؤلفون: | Rui Li, Guisen Fan, Xiao Ouyang, Guojun Wang, Hao Wei |
المصدر: | Composites & Advanced Materials; Jan-Dec2021, Vol. 30, p1-12, 12p |
مصطلحات موضوعية: | MECHANICAL behavior of materials, EPOXY resins, DAMPING (Mechanics), DYNAMIC mechanical analysis, MICROSPHERES |
مستخلص: | Composite foams with 10--50 vol% hollow polymeric microspheres were prepared using bisphenol A epoxy resin and polyetheramine curing agent as the matrix. The results demonstrated that the density, hardness, and static mechanical properties of the epoxy resin/hollow polymer microsphere composite foams, as well as their dynamic mechanical properties under forced non-resonance, were similar to those of polymer/hollow glass microsphere composite foams. At 25 °C and under 1--100 Hz forced resonance, the first-order and second-order resonance frequencies of the composite foams shifted to the low-frequency region as the volume fraction of hollow polymer microspheres increased. Meanwhile, the first-order and second-order loss factors of the as-prepared composite foams were improved by 41.7% and 103.3%, respectively, compared with the pure epoxy resin. Additionally, the first-order and second-order loss factors of the asprepared composite foams reached a maximum at 40 vol% and 30 vol% hollow polymer microspheres, respectively. This research helps us to expand the application range of composite foam materials in damping research. [ABSTRACT FROM AUTHOR] |
Copyright of Composites & Advanced Materials is the property of Sage Publications Inc. and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) | |