Measurement of Thermal Stress by X-ray Nano-Diffraction in (111)-Oriented Nanotwinned Cu Bumps for Cu/SiO 2 Hybrid Joints. |
المؤلفون: |
Hsu, Wei-You, Yang, Shih-Chi, Lin, You-Yi, Hsieh, Wan-Zhen, Tu, King-Ning, Chiu, Wei-Lan, Chang, Hsiang-Hung, Chiang, Ching-Yu, Chen, Chih |
المصدر: |
Nanomaterials (2079-4991); Sep2023, Vol. 13 Issue 17, p2448, 16p |
مصطلحات موضوعية: |
COPPER, HYBRID securities, X-rays, THERMAL expansion, SYNCHROTRON radiation |
مستخلص: |
X-ray nanodiffraction was used to measure the thermal stress of 10 µm nanotwinned Cu bumps in Cu/SiO2 hybrid structures at −55 °C, 27 °C, 100 °C, 150 °C, and 200 °C. Bonding can be achieved without externally applied compression. The X-ray beam size is about 100 nm in diameter. The Cu bump is dominated by (111) oriented nano-twins. Before the hybrid bonding, the thermal stress in Cu bumps is compressive and remains compressive after bonding. The average stress in the bonded Cu joint at 200 °C is as large as −169.1 MPa. In addition, using the strain data measured at various temperatures, one can calculate the effective thermal expansion coefficient (CTE) for the 10 µm Cu bumps confined by the SiO2 dielectrics. This study reports a useful approach on measuring the strain and stress in oriented metal bumps confined by SiO2 dielectrics. The results also provide a deeper understanding on the mechanism of hybrid bonding without externally applied compression. [ABSTRACT FROM AUTHOR] |
|
Copyright of Nanomaterials (2079-4991) is the property of MDPI and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |