Fracture Resistance and Failure Mode of Monolithic Zirconia, Veneered Zirconia, and Metal-Ceramic Full-Coverage Restorations: A Comparative In Vitro Study.
العنوان: | Fracture Resistance and Failure Mode of Monolithic Zirconia, Veneered Zirconia, and Metal-Ceramic Full-Coverage Restorations: A Comparative In Vitro Study. |
---|---|
المؤلفون: | Almohammed, Saleh N., Dourado, Annalita M., Quran, Firas A. Al |
المصدر: | International Journal of Prosthodontics; 2024, Vol. 37 Issue 1, p80-91, 12p |
مصطلحات موضوعية: | FAILURE mode & effects analysis, ZIRCONIUM oxide, HYBRID materials, COMPRESSION loads, FRACTURE strength |
مستخلص: | Purpose: To evaluate and compare the fracture mode and strength of monolithic zirconia to veneered zirconia and metal-ceramic full-coverage restorations following artificial aging and to test the performance of translucent zirconia in terms of load-bearing capacity. Materials and Methods: Two mandibular first molars were prepared and scanned for their respective groups of full-coverage restorations. A total of 75 fullcoverage restorations were fabricated and divided into five groups: two groups for monolithic zirconia, two groups for veneered zirconia, and one group for metal-ceramic. Then, 75 light-cured hybrid composite resin dies were fabricated to serve as abutments. Before cementation, all full-coverage restorations were subjected to accelerated aging. After cementation, all full-coverage restorations were subjected to compressive loading until fracture in an electromechanical universal testing machine. A two-way nested ANOVA and Tukey test were used to analyze the results with 95% confidence levels. Results: Monolithic zirconia full-coverage restorations showed the highest mean fracture resistance of 4,201.0 N, followed by metalceramic full-coverage restorations of 3,609.3 N, and veneered zirconia full-coverage restorations showed the lowest mean fracture resistance of 2,524.6 N. The main mode of failure was cohesive bulk fracture for the monolithic zirconia group, cohesive/adhesive failure with infrastructure damage for the veneered zirconia group, and cohesive/adhesive failure without infrastructure damage for the metal-ceramic group. Conclusions: Monolithic zirconia full-coverage restorations showed superior resistance to fracture compared to metal-ceramic full-coverage restorations and are highly reliable in terms of load-bearing capacity within the posterior regions of the mouth. [ABSTRACT FROM AUTHOR] |
Copyright of International Journal of Prosthodontics is the property of Quintessence Publishing Company Inc. and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) | |