Comparison of Hashin and Puck criterions for failure behavior of pin loaded composite plates. |
| المؤلفون: |
Dogan, C., Kaman, M. O., Erdem, S., Albayrak, M. |
| المصدر: |
Materialwissenschaft und Werkstoffechnik; Mar2024, Vol. 55 Issue 3, p314-329, 16p |
| مصطلحات موضوعية: |
COMPOSITE plates, CARBON composites, FIBROUS composites, TENSILE tests, CARBON fibers, LAMINATED materials |
| مستخلص: |
In this study, the failure behavior of carbon fiber‐reinforced pin‐jointed composite plates were analyzed for different criteria. For this purpose, composite plates with a single and double pin joints were prepared from four layers carbon fiber composites. The effect of pin number, pin position on plate damage load and type was investigated experimentally and numerically under the tensile test. Numerically, progressive damage analysis was performed using Hashin and Puck failure criteria, and the approach rates to the experimental results were determined. It was observed that the experimental results obtained for single pin joint composites and the numerical data obtained using the Puck damage criterion were at least 87 % compatible, and this rate was determined as 85 % for the Hashin failure criterion. For the double pin jointed composites, it was seen that the experimental results and the results of the Puck damage criterion were compatible with at least 90 %, and this rate was obtained as 84 % for the Hashin failure criterion. The dominant damage type seen in the specimen is matrix shear and fiber compression according to the Hashin damage criterion, inter fiber failure in transverse tension for Puck. [ABSTRACT FROM AUTHOR] |
|
Copyright of Materialwissenschaft und Werkstoffechnik is the property of Wiley-Blackwell and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |