التفاصيل البيبلوغرافية
| العنوان: |
Enhancement of spin–orbit torque and magnetization switching by Pt100–xWx alloy in Co-based films. |
| المؤلفون: |
Liang, Hongming, Li, Kuo, Xu, Mingyang, Zhang, Yao, Liu, Peiqiao, Wang, Sizhe, Sun, Zhiwen, Yang, Ruizhi, Yu, Guanghua, Li, Minghua |
| المصدر: |
Journal of Applied Physics; 4/28/2024, Vol. 135 Issue 16, p1-9, 9p |
| مصطلحات موضوعية: |
PERPENDICULAR magnetic anisotropy, TUNGSTEN alloys, MAGNETIZATION, HEAVY metals, ALLOYS, TORQUE, HEUSLER alloys, TANTALUM |
| مستخلص: |
Alloying heavy metals (HMs) has been an effective method for enhancing the efficiency of spin–orbit torque. In this study, we demonstrate that Pt100−xWx/Pt/Co/Ta multilayers still maintain perpendicular magnetic anisotropy after high-temperature annealing. Doping tungsten (W) into HM platinum (Pt) at the bottom of a Pt/Co/Ta multilayer significantly increases the spin Hall angle (θ S H ) and reduces the critical switching current density (Jc). The harmonic Hall test results show that the θ S H of the Pt88W12 alloy film is approximately 0.29, which is higher than that of the pure Pt film (0.15). The magnetization switching test reveals that the Jc of Pt94W6 alloy film is approximately 4.892 × 106 A/cm2, which is 51.9% lower than that of the pure Pt film. This study offers a valuable method for reducing power consumption and enhancing the efficiency of related application devices. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Applied Physics is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |
Find this article in full text from Scitation.