Improvement of the Sintering and Mechanical Properties of SiC Utilizing the Increased Milling Efficiency of Si Source Recycled from Si Sludge. |
| المؤلفون: |
Hanjung Kwon, Jaemin Song, Doyeon Lee, Jonghyuck Jeon, Jin-Young Lee |
| المصدر: |
Materials Transactions; 2024, Vol. 65 Issue 4, p440-446, 7p |
| مصطلحات موضوعية: |
SINTERING, GRAIN size, RAW materials, INDUSTRIAL costs, MICROSTRUCTURE, POWDERS |
| مستخلص: |
This study enhanced the efficiency in the milling process of preparing SiC powder using the source recycled from Si sludge as a raw material. The sludge, which is formed during machining Si wafer, intrinsically contains SiC (abrasive material), thus due to the high hardness of SiC, the milling effect on the Si sources with sludge was expected to be higher than that of the pure Si. Indeed, the SiC included intrinsically in the sludge resulted in more effective milling of the sludge--carbon mixture; and after high-energy ball milling, the crystallite size of Si in the mixture decreased to 26.8 nm, while the crystallite size of Si in the source without sludge was 49.5 nm. The increase of milling effect in the sludge contributed to the low reaction temperature, improved the sinterability, and reduced the grain size of the sintered SiC. Finally, using the sludge as a raw material, SiC of high density, refined microstructure, and enhanced hardness (Hv: 29.5 GPa, previously reported Hv: (23.7-26) GPa) was obtained. These results suggest that the use of sludge can be an effective way to produce SiC with refined microstructure and enhanced properties, as well as to reduce the cost of production of SiC parts. [ABSTRACT FROM AUTHOR] |
|
Copyright of Materials Transactions is the property of Japan Institute of Metals & Materials and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |