Determining the Influence of Curing Temperature and SCMs on C-A-S-H Composition Using SEM-EDS Hypermaps.
| العنوان: | Determining the Influence of Curing Temperature and SCMs on C-A-S-H Composition Using SEM-EDS Hypermaps. |
|---|---|
| المؤلفون: | Hemstad, Petter, Kjellemyr, Petter, Weerdt, Klaartje De |
| المصدر: | Nordic Concrete Research; Jun2024, Vol. 70 Issue 1, p125-146, 22p |
| مصطلحات موضوعية: | FLY ash, SCANNING electron microscopy, CALCIUM, PORTLAND cement, POZZUOLANAS |
| مستخلص: | Calcium-alumina-silicate-hydrate (C-A-S-H) is the main hydration product formed in Portland composite cement pastes. C-A-S-H is a key phase with regard to the strength and durability of concrete. Proper characterization of C-A-S-H is difficult due to intermixing with other phases, thus limiting the applicability of point scan analyses using scanning electron microscopy (SEM). Recent advances have enabled the use of hypermaps from energy dispersive spectroscopy (EDS) to investigate hydrate phases with better statistics. This study investigated how increased curing temperature and the inclusion of pozzolanic SCMs change the composition of the C-A-S-H, using the edxia plugin and SEM-EDS hypermaps. Composite cement pastes were cured at 20, 38, and 60°C for 180 days before analysis. We discuss the interpretation of the data from hypermaps in comparison to the traditional point scan approach. [ABSTRACT FROM AUTHOR] |
| Copyright of Nordic Concrete Research is the property of Sciendo and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) | |
| قاعدة البيانات: | Complementary Index |
Full Text Finder كن أول من يترك تعليقا!