Rapid Microwave Synthesis, Characterization and Reactivity of Lithium Nitride Hydride, Li4NH. |
| المؤلفون: |
Tapia-Ruiz, Nuria, Sorbie, Natalie, Vaché, Nicolas, Hoang, Tuan K. A., Gregory, Duncan H. |
| المصدر: |
Materials (1996-1944); Nov2013, Vol. 6 Issue 11, p5410-5426, 17p |
| مصطلحات موضوعية: |
LITHIUM nitrides, LITHIUM hydride, MICROWAVES, X-ray diffraction, LITHIUM carbonate, STOICHIOMETRY, NONSTOICHIOMETRIC compounds |
| مستخلص: |
Lithium nitride hydride, Li4NH, was synthesised from lithium nitride and lithium hydride over minute timescales, using microwave synthesis methods in the solid state for the first time. The structure of the microwave-synthesised powders was confirmed by powder X-ray diffraction [tetragonal space group I41/a; a = 4.8864(1) Å, c = 9.9183(2) Å] and the nitride hydride reacts with moist air under ambient conditions to produce lithium hydroxide and subsequently lithium carbonate. Li4NH undergoes no dehydrogenation or decomposition [under Ar(g)] below 773 K. A tetragonal-cubic phase transition, however, occurs for the compound at ca. 770 K. The new high temperature (HT) phase adopts an anti-fluorite structure (space group Fm 3 m; a = 4.9462(3) Å) with N3- and H- ions disordered on the 4a sites. Thermal treatment of Li4NH under nitrogen yields a stoichiometric mixture of lithium nitride and lithium imide (Li3N and Li2NH respectively). [ABSTRACT FROM AUTHOR] |
|
Copyright of Materials (1996-1944) is the property of MDPI and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |
Full Text Finder