Mechanical and Interfacial Characterization of Jute Fabrics Reinforced Unsaturated Polyester Resin Composites
العنوان: | Mechanical and Interfacial Characterization of Jute Fabrics Reinforced Unsaturated Polyester Resin Composites |
---|---|
المؤلفون: | Ruhul A. Khan, Harun Ar Rashid, Kamrun N. Keya, Farjana A. Koly, Md. Naimul Islam, Shahirin Shahida, Farhana Islam, Nanda Karmaker, Jumana Mahmud |
المصدر: | Nano Hybrids and Composites. 25:22-31 |
بيانات النشر: | Trans Tech Publications, Ltd., 2019. |
سنة النشر: | 2019 |
مصطلحات موضوعية: | 020303 mechanical engineering & transports, Materials science, 0203 mechanical engineering, Resin composite, Unsaturated polyester, 02 engineering and technology, Composite material, 021001 nanoscience & nanotechnology, 0210 nano-technology, Characterization (materials science) |
الوصف: | Jute fabrics reinforced Unsaturated Polyester Resin (UPR)-based composites were prepared by conventional hand lay-up technique. Different proportions (5 to 50% by weight) of fibre content was used in preparation of the composite. Tensile Strength (TS), Tensile Modulus (TM), Bending Modulus (BM), Bending Strength (BS), Impact Strength (IS) of the fabricated composites were studied. Upon each addition of fiber content in the matrix, mechanical properties of the composites were increased. The Tensile Strength (TS) of the 5% and 50% fiber reinforced composites was 18 MPa and 42 MPa respectively. Scanning Electron Microscopy (SEM) showed interfacial properties of the composites and it was revealed that the bond between fiber and matrix was excellent. |
تدمد: | 2297-3400 |
URL الوصول: | https://explore.openaire.eu/search/publication?articleId=doi_________::43cb314407b54fe4c6d486bbe62445f1 https://doi.org/10.4028/www.scientific.net/nhc.25.22 |
حقوق: | CLOSED |
رقم الأكسشن: | edsair.doi...........43cb314407b54fe4c6d486bbe62445f1 |
قاعدة البيانات: | OpenAIRE |
كن أول من يترك تعليقا!