Microstructural, microscratch and nanohardness mechanical characterization of secondary commercial HPDC AlSi9Cu3-type alloy
| العنوان: | Microstructural, microscratch and nanohardness mechanical characterization of secondary commercial HPDC AlSi9Cu3-type alloy |
|---|---|
| المؤلفون: | Octavio Lozada Flores, Gabriel Rodríguez Ortiz, Gerardo Altamirano Guerrero, José Reyes Gasga, Patricia Sheilla Costa, Antonio Enrique Salas Reyes, Jaime Francisco García Robledo |
| المصدر: | Journal of Materials Research and Technology, Vol 9, Iss 4, Pp 8266-8282 (2020) |
| بيانات النشر: | Elsevier BV, 2020. |
| سنة النشر: | 2020 |
| مصطلحات موضوعية: | lcsh:TN1-997, Gas porosity, Materials science, Alloy, Population, Intermetallic, High-Pressure die casting, 02 engineering and technology, engineering.material, (Cu-Fe-Si-Mg) high contents, 01 natural sciences, Biomaterials, AlSi9Cu3-type alloy, 0103 physical sciences, Composite material, education, lcsh:Mining engineering. Metallurgy, Shrinkage, 010302 applied physics, education.field_of_study, Precipitation (chemistry), Metals and Alloys, Microstructural characterization, 021001 nanoscience & nanotechnology, Die casting, Surfaces, Coatings and Films, Intermetallic compounds, Volume fraction, Micro and nanomechanical testing, Ceramics and Composites, engineering, 0210 nano-technology |
| الوصف: | A key issue in producing high quality aluminum automotive components using High-Pressure Die Casting (HPDC) process is minimizing the amount of imperfections. In the present research work, by means of optical microscopy (OM), SEM, TEM and AFM characterization techniques, microstructural evolution of secondary commercial HPDC AlSi9Cu3-type alloy was studied. For this purpose, one Al-alloy called C1 containing nominal composition and a second one called C2 going out of specification were employed. In addition to metallographic characterization, Vickers and nanohardness and microscratch mechanical testing techniques were applied to analyze material behavior. Furthermore, complementary thermodynamic calculations were done to estimate alloy phases precipitation as function of temperature. Results indicate that globular and ramified dendrites are developed in C1 and C2 Al-alloys, respectively, due the major solidification time between them. In fact, gas porosity and shrinkage microporosity were detected. α-Fe particle increased in size but not in volume fraction, as Al2Cu and β-Fe intermetallics do. Mostly, it was found that α-Fe particle growth following a coring behavior, formed by nanospherical particles. Thus, main shrinkage microporosity is associated with Al2Cu precipitate, where shrinkage pores in alloy C2 present several nanoparticles located between dendrite arms, identify by SEM and TEM analysis. Finally, hardness of alloys differs in 30 HV values due intermetallics population, whereas nanohardness allowed measuring single value of each phase. Because no major nanohardness differences were observed, microscratch resistance behaves similar in both alloys. Hence, present microstructural/mechanical characterization results can be taken into account for redesign and improving commercial HPDC Al-components. |
| تدمد: | 2238-7854 |
| URL الوصول: | https://explore.openaire.eu/search/publication?articleId=doi_dedup___::791196eb6b55fb2f0595e0e8ae181125 https://doi.org/10.1016/j.jmrt.2020.05.098 |
| حقوق: | OPEN |
| رقم الأكسشن: | edsair.doi.dedup.....791196eb6b55fb2f0595e0e8ae181125 |
| قاعدة البيانات: | OpenAIRE |