Influence of the coating brittleness on the thermomechanical fatigue behavior of a $\beta$-NiAl coated R125 Ni-based superalloy
العنوان: | Influence of the coating brittleness on the thermomechanical fatigue behavior of a $\beta$-NiAl coated R125 Ni-based superalloy |
---|---|
المؤلفون: | Billard, Capucine, Texier, Damien, Rambaudon, Matthieu, Teissedre, Jean-Christophe, Bourhila, Noureddine, Marquie, Dimitri, Marcin, Lionel, Singer, Hugo, Maurel, Vincent |
سنة النشر: | 2024 |
المجموعة: | Condensed Matter Physics (Other) |
مصطلحات موضوعية: | Condensed Matter - Materials Science, Physics - Applied Physics |
الوصف: | The brittleness of an aluminide diffusion coating protecting a Ren\'e 125 Ni-based polycrystalline superalloy was investigated over a wide range of temperatures in its as-received and thermally aged form. Isothermal and thermal cycled aging were performed on the coated system at a maximum temperature of 1100 {\deg}C. Microstructure evolutions and damage initiation within the coating were characterized. Interrupted tensile tests and thermomechanical fatigue tests were conducted to document critical stress-strain conditions leading to the coating cracking and lifetime for the case of thermo-mechanical fatigue loading. Advanced digital image correlation and acoustic emission techniques were used to detect coating cracking. Isothermal oxidation or cyclic oxidation led to improved strain-to-failure due to metallurgical evolutions and also longer fatigue life under thermomechanical fatigue conditions. |