Preparation of mono-dispersed, high energy release, core/shell structure Al nanopowders and their application in HTPB propellant as combustion enhancers

التفاصيل البيبلوغرافية
العنوان: Preparation of mono-dispersed, high energy release, core/shell structure Al nanopowders and their application in HTPB propellant as combustion enhancers
المؤلفون: Fengyi Wang, Zhiguo Wu, Xushui Shangguan, Yunqiang Sun, Juanjuan Feng, Zhongyou Li, Luyang Chen, Shiyong Zuo, Renfu Zhuo, Pengxun Yan
المصدر: Scientific Reports, Vol 7, Iss 1, Pp 1-9 (2017)
بيانات النشر: Nature Portfolio, 2017.
سنة النشر: 2017
المجموعة: LCC:Medicine
LCC:Science
مصطلحات موضوعية: Medicine, Science
الوصف: Abstract Mono-dispersed, spherical and core/shell structure aluminum nanopowders (ANPs) were produced massively by high energy ion beam evaporation (HEIBE). And the number weighted average particle size of the ANPs is 98.9 nm, with an alumina shell (3–5 nm). Benefiting from the passivation treatment, the friction, impact and electrostatic spark sensitivity of the ANPs are almost equivalent to those of aluminum micro powders. The result of TG-DSC indicates the active aluminum content of ANPs is 87.14%, the enthalpy release value is 20.37 kJ/g, the specific heat release S 1/Δm 1* (392–611 °C) which determined the ability of energy release is 19.95 kJ/g. And the value of S 1/Δm 1* is the highest compared with ANPs produced by other physical methods. Besides, the ANPs perfectly compatible with hydroxyl-terminated polybutadiene (HTPB), 3 wt. % of ANPs were used in HTPB propellant replaced micron aluminum powders, and improved the burning rate in the 3–12 MPa pressure range and reduced the pressure exponential by more than 31% in the 3–16 MPa pressure range. The production technology of ANPs with excellent properties will greatly promote the application of ANPs in the field of energetic materials such as propellant, explosive and pyrotechnics.
نوع الوثيقة: article
وصف الملف: electronic resource
اللغة: English
تدمد: 2045-2322
Relation: https://doaj.org/toc/2045-2322
DOI: 10.1038/s41598-017-05599-0
URL الوصول: https://doaj.org/article/0aad586e96cb48b1a445b8521b7a6e12
رقم الأكسشن: edsdoj.0aad586e96cb48b1a445b8521b7a6e12
قاعدة البيانات: Directory of Open Access Journals
الوصف
تدمد:20452322
DOI:10.1038/s41598-017-05599-0