Crystal Structure and Properties of Gd1-xSrxCo1-yFeyO3-δ Oxides as Promising Materials for Catalytic and SOFC Application
العنوان: | Crystal Structure and Properties of Gd1-xSrxCo1-yFeyO3-δ Oxides as Promising Materials for Catalytic and SOFC Application |
---|---|
المؤلفون: | Tatiana V. Aksenova, Darya K. Mysik, Vladimir A. Cherepanov |
المصدر: | Catalysts, Vol 12, Iss 11, p 1344 (2022) |
بيانات النشر: | MDPI AG, 2022. |
سنة النشر: | 2022 |
المجموعة: | LCC:Chemical technology LCC:Chemistry |
مصطلحات موضوعية: | solid solution, X-ray diffraction, crystal structure, thermogravimetric analysis, oxygen nonstoichiometry, conductivity, Chemical technology, TP1-1185, Chemistry, QD1-999 |
الوصف: | A series of samples with the overall composition Gd1-xSrxCo1-yFeyO3-δ (x = 0.8; 0.9 and 0.1 ≤ y ≤ 0.9), which are promising materials for catalytic and SOFC application, was prepared by a glycerol nitrate technique. X-ray diffraction analysis allowed to describe Gd0.2Sr0.8Co1-yFeyO3-δ with 0.1 ≤ y ≤ 0.5 in a tetragonal 2ap × 2ap × 4ap superstructure (SG I4/mmm), while oxides with 0.6 ≤ y ≤ 0.9 exhibit cubic disordered perovskite structure (SG Pm-3m). All Gd0.1Sr0.9Fe1-yCoyO3-δ oxides within the composition range 0.1 ≤ y ≤ 0.9 possess the cubic perovskite structure (SG Pm-3m). The structural parameters were refined using the Rietveld full-profile method. The changes of oxygen content in Gd1-xSrxCo1-yFeyO3-δ versus temperature were determined by thermogravimetric analysis. The introduction of iron into the cobalt sublattice leads to a gradual increase in the unit cell parameters and unit cell volume, accompanied with increasing oxygen content. The temperature dependency of conductivity for Gd0.2Sr0.8Co0.3Fe0.7O3-δ exhibits a maximum (284 S/cm) at ≈600 K in air. The positive value of the Seebeck coefficient indicates predominant p-type conductivity in the Gd0.2Sr0.8Co0.3Fe0.7O3-δ complex oxide. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 2073-4344 |
Relation: | https://www.mdpi.com/2073-4344/12/11/1344; https://doaj.org/toc/2073-4344 |
DOI: | 10.3390/catal12111344 |
URL الوصول: | https://doaj.org/article/30c16ffdcdba4d35959ddceaa61091f4 |
رقم الأكسشن: | edsdoj.30c16ffdcdba4d35959ddceaa61091f4 |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 20734344 |
---|---|
DOI: | 10.3390/catal12111344 |