Mechanical and Anticorrosive Properties of Graphene/Epoxy Resin Composites Coating Prepared by in-Situ Method
العنوان: | Mechanical and Anticorrosive Properties of Graphene/Epoxy Resin Composites Coating Prepared by in-Situ Method |
---|---|
المؤلفون: | Zhiyi Zhang, Wenhui Zhang, Diansen Li, Youyi Sun, Zhuo Wang, Chunling Hou, Lu Chen, Yang Cao, Yaqing Liu |
المصدر: | International Journal of Molecular Sciences, Vol 16, Iss 1, Pp 2239-2251 (2015) |
بيانات النشر: | MDPI AG, 2015. |
سنة النشر: | 2015 |
المجموعة: | LCC:Biology (General) LCC:Chemistry |
مصطلحات موضوعية: | graphene, epoxy resin, composite coating, mechanical properties, erosion resistance, Biology (General), QH301-705.5, Chemistry, QD1-999 |
الوصف: | The graphene nanosheets-based epoxy resin coating (0, 0.1, 0.4 and 0.7 wt %) was prepared by a situ-synthesis method. The effect of polyvinylpyrrolidone/reduced graphene oxide (PVP-rGO) on mechanical and thermal properties of epoxy resin coating was investigated using nanoindentation technique and thermogravimetric analysis, respectively. A significant enhancement (ca. 213% and 73 °C) in the Young modulus and thermal stability of epoxy resin coating was obtained at a loading of 0.7 wt %, respectively. Furthermore, the erosion resistance of graphene nanosheets-based epoxy resin coating was investigated by electrochemical measurement. The results showed also that the Rrcco (ca. 0.3 mm/year) of graphene nanosheets-based epoxy resin coating was far lower than neat epoxy resin (1.3 mm/year). Thus, this approach provides a novel route for improving erosion resistance and mechanical-thermal stability of polymers coating, which is expected to be used in mechanical-thermal-corrosion coupling environments. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 1422-0067 |
Relation: | http://www.mdpi.com/1422-0067/16/1/2239; https://doaj.org/toc/1422-0067 |
DOI: | 10.3390/ijms16012239 |
URL الوصول: | https://doaj.org/article/67ac6c0c8a21406099f18960100375b1 |
رقم الأكسشن: | edsdoj.67ac6c0c8a21406099f18960100375b1 |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 14220067 |
---|---|
DOI: | 10.3390/ijms16012239 |