Investigation on microstructure, hardness, wear behavior and fracture surface analysis of Strontium (Sr) and Calcium (Ca) content A357 modified alloy by statistical technique
العنوان: | Investigation on microstructure, hardness, wear behavior and fracture surface analysis of Strontium (Sr) and Calcium (Ca) content A357 modified alloy by statistical technique |
---|---|
المؤلفون: | K. Ganesh, K. Hemachandra Reddy, S. Sudhakar Babu, R. Suresh |
المصدر: | Frattura ed Integrità Strutturale, Vol 17, Iss 65, Pp 32-46 (2023) |
بيانات النشر: | Gruppo Italiano Frattura, 2023. |
سنة النشر: | 2023 |
المجموعة: | LCC:Mechanical engineering and machinery LCC:Structural engineering (General) |
مصطلحات موضوعية: | a357 alloy, strontium (sr), calcium (ca), stir casting, hardness, wear behavior, fracture surface, statistical technique, Mechanical engineering and machinery, TJ1-1570, Structural engineering (General), TA630-695 |
الوصف: | The aluminum alloy are extensively used in several industrial applications. Stir casting is one of the most frequently accepted methods. In the present investigation, how the microstructure, mechanical and wear mechanics of A357 alloy were impacted by the presence of Sr/Ca was investigated. The outcomes revealed that addition of elements (Sr/Ca) enhance the microstructural features. Uniform dispersal of particulates (Sr/ Ca) in Al357 alloy and also the modified structure of silicon (Si) were observed. Hardness of modified alloy was evaluated by using hardness tester. A result reveals that hardness of modified alloy was improved by increasing in the Sr/Ca content. The wear rate of modified alloy was evaluated by using Pin and Disc wear test rig. Test trials were conducted according to Taguchi technique. L27 array was implemented for evaluation of data. The effect of varying parameters (factors) on wear loss and COF were analyzed using ANOVA (Analysis of Variance) method. ANOVA outcomes shown that, the Sr/Ca content has a better significant impact on wear behavior and COF of the modified alloy. A wear fractography result shows the internal fracture structure of a wornout surface which was studied by SEM analysis. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 1971-8993 |
Relation: | https://www.fracturae.com/index.php/fis/article/view/4108/3813; https://doaj.org/toc/1971-8993 |
DOI: | 10.3221/IGF-ESIS.65.03 |
URL الوصول: | https://doaj.org/article/81e5ce83dff6489abba4e42d2c3100d5 |
رقم الأكسشن: | edsdoj.81e5ce83dff6489abba4e42d2c3100d5 |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 19718993 |
---|---|
DOI: | 10.3221/IGF-ESIS.65.03 |