Microwave Sintering of SiAlON Ceramics with TiN Addition
العنوان: | Microwave Sintering of SiAlON Ceramics with TiN Addition |
---|---|
المؤلفون: | Özgür Sevgi Canarslan, Roberto Rosa, Levent Köroğlu, Erhan Ayas, Alpagut Kara, Paolo Veronesi |
المصدر: | Materials, Vol 12, Iss 8, p 1345 (2019) |
بيانات النشر: | MDPI AG, 2019. |
سنة النشر: | 2019 |
المجموعة: | LCC:Technology LCC:Electrical engineering. Electronics. Nuclear engineering LCC:Engineering (General). Civil engineering (General) LCC:Microscopy LCC:Descriptive and experimental mechanics |
مصطلحات موضوعية: | SiAlON composites, microwave sintering, 2.45 GHz, single mode cavity, susceptor, Technology, Electrical engineering. Electronics. Nuclear engineering, TK1-9971, Engineering (General). Civil engineering (General), TA1-2040, Microscopy, QH201-278.5, Descriptive and experimental mechanics, QC120-168.85 |
الوصف: | α-β SiAlON/TiN composites with nominal composition of α:β = 25:75 were fabricated by microwave sintering. The effect of titanium nitride addition on the phases, microstructure, microwave absorption ability and mechanical properties (Vickers hardness and fracture toughness) of the SiAlON-based composites were studied. Finite Difference Time Domain (FDTD) software was used for the numerical simulation in order to assess the most suitable experimental setup. Sintering trials were performed in a single mode microwave furnace operating at 2.45 GHz and a power output of 660 W, for a reaction time of 30 min. SiC blocks were used as a susceptor to accelerate the microwave processing by hybrid heating, with reduced heat losses from the surface of the material of the α-β SiAlON/TiN composites. The optimum comprehensive mechanical properties, corresponding to a relative density of 96%, Vickers hardness of 12.98 ± 1.81 GPa and Vickers indentation fracture toughness of 5.52 ± 0.71 MPa.m1/2 were obtained at 850 °C when the content of TiN was 5 wt.%. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 1996-1944 12081345 |
Relation: | https://www.mdpi.com/1996-1944/12/8/1345; https://doaj.org/toc/1996-1944 |
DOI: | 10.3390/ma12081345 |
URL الوصول: | https://doaj.org/article/b8c56d1f01714cd7bc74badd6a82f15e |
رقم الأكسشن: | edsdoj.b8c56d1f01714cd7bc74badd6a82f15e |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 19961944 12081345 |
---|---|
DOI: | 10.3390/ma12081345 |