Synthesis of rGO/CoFe2O4 Composite and Its Magnetorheological Characteristics
العنوان: | Synthesis of rGO/CoFe2O4 Composite and Its Magnetorheological Characteristics |
---|---|
المؤلفون: | Yang Lv, Chengjie Gong, Yuzhen Dong, Hyoung Jin Choi |
المصدر: | Materials, Vol 17, Iss 8, p 1859 (2024) |
بيانات النشر: | MDPI AG, 2024. |
سنة النشر: | 2024 |
المجموعة: | LCC:Technology LCC:Electrical engineering. Electronics. Nuclear engineering LCC:Engineering (General). Civil engineering (General) LCC:Microscopy LCC:Descriptive and experimental mechanics |
مصطلحات موضوعية: | rGO, CoFe2O4, composite, magnetorheological, yield stress, Technology, Electrical engineering. Electronics. Nuclear engineering, TK1-9971, Engineering (General). Civil engineering (General), TA1-2040, Microscopy, QH201-278.5, Descriptive and experimental mechanics, QC120-168.85 |
الوصف: | In this study, composite particles of rGO/CoFe2O4 were synthesized using a solvothermal method to fabricate a low-density magnetorheological (MR) material with enhanced sedimentation stability. The morphology and crystallographic features of rGO/CoFe2O4 were characterized via SEM, TEM, and XRD, and its magnetic properties were tested using VSM. The MR fluid was formulated by blending rGO/CoFe2O4 particles into silicone oil. Under different magnet strengths (H), a rotational rheometer was used to test its MR properties. Typical MR properties were observed, including shear stress, viscosity, storage/loss modulus, and dynamic yield stress (τdy) following the Herschel–Bulkley model reaching 200 Pa when H is 342 kA/m. Furthermore, the yield stress of the MR fluid follows a power law relation as H increases and the index changes from 2.0 (in the low H region) to 1.5 (in the high H region). Finally, its MR efficiency was calculated to be about 104% at H of 342 kA/m. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 1996-1944 |
Relation: | https://www.mdpi.com/1996-1944/17/8/1859; https://doaj.org/toc/1996-1944 |
DOI: | 10.3390/ma17081859 |
URL الوصول: | https://doaj.org/article/f466597a7cf6480280ce69009d23a145 |
رقم الأكسشن: | edsdoj.f466597a7cf6480280ce69009d23a145 |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 19961944 |
---|---|
DOI: | 10.3390/ma17081859 |