As part of a pre-flight ground based investigation of crystal growth of II-VI compound semiconductors, a number of ZnSe boules have been grown by physical vapor transport (PVT) at Marshall Space Flight Center. Boules were grown in both horizontal and vertical configurations and seeded and self-seeded growth techniques were employed. As-grown and/or cleaved boules were examined by a combination of synchrotron white beam x-ray topography (SWBXT) and high resolution triple axis diffraction (HRTXD) to characterized the structural defects and correlate them with the growth conditions. Horizontal grown boules tend to grow away from the ampoule wall (contactless growth) and generally exhibit large (110) facets parallel to the gravity vector. Vertical grown boules grew to the full diameter of the ampoule and exhibited no faceting. X-ray topography combined with back reflection x-ray diffraction revealed the presence of lamellar twins (180 deg type about the [111] axis) in horizontal grown boules while vertically grown boules contain a few large grains, some of which are twinned. X-ray topographs and reciprocal space maps recorded from the boules show the better crystal quality of horizontal grown boules. The relationship between crystal quality and gravity vector is investigated. Further, an attempt is made to extend the Hurle theory of twin nucleation in Czochralski grown crystals to explain the twinning mechanisms in horizontal grown boules.