Effect of laser etching on surface characteristics and porcelain bond to soft milled and direct metal laser sintered cobalt chromium alloys.
| العنوان: | Effect of laser etching on surface characteristics and porcelain bond to soft milled and direct metal laser sintered cobalt chromium alloys. |
|---|---|
| المؤلفون: | AboElhassan RG; Lecturer, Fixed Prosthodontics, Department of Conservative Dentistry, Alexandria University, Alexandria, Egypt., Morsy N; Lecturer, Fixed Prosthodontics, Department of Conservative Dentistry, Alexandria University, Alexandria, Egypt. Electronic address: nohamorsy.nm88@yahoo.com. |
| المصدر: | The Journal of prosthetic dentistry [J Prosthet Dent] 2024 Jul; Vol. 132 (1), pp. 269.e1-269.e6. Date of Electronic Publication: 2024 Apr 11. |
| نوع المنشور: | Journal Article |
| اللغة: | English |
| بيانات الدورية: | Publisher: Mosby-Year Book Country of Publication: United States NLM ID: 0376364 Publication Model: Print-Electronic Cited Medium: Internet ISSN: 1097-6841 (Electronic) Linking ISSN: 00223913 NLM ISO Abbreviation: J Prosthet Dent Subsets: MEDLINE |
| أسماء مطبوعة: | Publication: St. Louis Mo : Mosby-Year Book Original Publication: St. Louis, Mosby. |
| مواضيع طبية MeSH: | Chromium Alloys*/chemistry , Surface Properties* , Dental Porcelain*/chemistry , Lasers, Solid-State* , Dental Bonding*/methods, Microscopy, Electron, Scanning ; Dental Etching/methods ; Wettability ; Microscopy, Atomic Force ; Materials Testing ; Dental Stress Analysis ; Humans ; In Vitro Techniques |
| مستخلص: | Statement of Problem: The surface topography of metal substrate can affect its bond to porcelain. A neodynium-doped yttrium aluminum garnet (Nd:YAG) laser has been introduced to modify the metal surface topography and improve porcelain bond strength. However, studies on the effect of laser etching on metal to porcelain bond strength are lacking. Purpose: The purpose of this in vitro study was to determine the effect of Nd:YAG laser etching on the surface roughness and wettability of and the porcelain bond strength to cobalt chromium (Co-Cr) substrate fabricated by milling and direct metal laser sintering (DMLS). Material and Methods: Thirty-two 0.5×3×25-mm Co-Cr specimens were fabricated by milling soft Co-Cr (M group) and DMLS Co-Cr metal powder (DML group). The surface topography of representative specimens from each study group was assessed under a scanning electron microscope (SEM) and an atomic force microscope (AFM). All specimens were assessed for surface roughness using a contact profilometer, and for wettability with a contact angle goniometer. Half of the specimens of each study group (n=8) were subjected to surface laser etching by using a Nd:YAG laser. The specimens subjected to etching were assessed again for surface topography and wettability. All specimens in both study groups were veneered with porcelain. The porcelain bond strength was tested with a 3-point bend test in a universal testing machine. The results were statistically analyzed with 2-way ANOVA test followed by the post hoc Tukey test for pairwise comparisons (α=.05). Results: After etching, the M group had a higher mean ±standard deviation Ra and Rz of 2.9 ±0.6 and 17.7 ±3.2 µm and significantly better wettability and bond strength of 79 ±6 and 52 ±13 MPa. In contrast, after etching, the DMLS group had a significantly lower Ra and Rz of 7.9 ±2.4 and 41.8 ±9.3 µm and significantly lower wettability and bond strength of 87 ±4 and 70 ±10 MPa. The DMLS group had a significantly higher roughness and bond strength than the M group before and after laser etching. The SEM and AFM showed different surface topography in the study groups. Conclusions: The manufacturing process of Co-Cr substrate had a significant effect on surface characteristics and porcelain bond strength. Laser etching improved the surface topography and bond strength of milled Co-Cr but not of DMLS Co-Cr. (Copyright © 2024 Editorial Council for The Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.) |
| المشرفين على المادة: | 0 (Chromium Alloys) 12001-21-7 (Dental Porcelain) |
| تواريخ الأحداث: | Date Created: 20240412 Date Completed: 20240703 Latest Revision: 20240703 |
| رمز التحديث: | 20240704 |
| DOI: | 10.1016/j.prosdent.2024.03.040 |
| PMID: | 38609765 |
| قاعدة البيانات: | MEDLINE |
Full Text via ClinicalKey 
Full Text Finder | تدمد: | 1097-6841 |
|---|---|
| DOI: | 10.1016/j.prosdent.2024.03.040 |