Surface Carbonization of GaN and the Related Structure Evolution during the Annealing Process. |
| المؤلفون: |
Jin-Long Liu, Liang-Xian Chen, Jun-Jun Wei, Li-Fu Hei, Xu Zhang, Cheng-Ming Li |
| المصدر: |
Chinese Physics Letters; Jan2018, Vol. 35 Issue 1, p1-1, 1p |
| مصطلحات موضوعية: |
CARBONIZATION, ANNEALING of metals, LUMINESCENCE, NUCLEATION, RAMAN spectroscopy |
| مستخلص: |
To explain the stabilization mechanism of the carbon-ion-implanted GaN under the diamond growth environment, the luminescence characteristics and structure evolution correlative with sites’ carbon atoms located for high-fluence carbon-ion-implanted GaN are discussed. GaN is implanted with carbon ion using fluence of 2 × 1017cm−2and energy of 45 keV. Then the implanted samples are annealed at 800°C for 20 min and 1 h under the N2atmosphere. The luminescence characteristics of carbon-ion-implanted GaN are evaluated by photoluminescence spectrum at wavelength 325 nm. The lattice damage of GaN is characterized by Raman spectrum and the corresponding vacancy-defect evolution before and after annealing is measured by slow positron annihilation. The results show that most of the carbon atoms will be located at the interstitial sites after carbon ion implantation due to the weak mobility. As the implanted samples are annealed, strong yellow luminescence is emitted and the vacancies for Ga (VGa) are reduced resulting from the migration of interstitial carbon (Ci) and formation of complexes (CGaand/or CGa-Ci) between them. As the annealing time is prolonged, the carbon ions accommodated by the vacancies are saturated, vacancy clusters with carbon atoms appear and the concentration of CGadiminishes, which will have an adverse effect on the diamond film nucleation and growth. [ABSTRACT FROM AUTHOR] |
|
Copyright of Chinese Physics Letters is the property of IOP Publishing and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |
Full Text Finder