Influence of Annealing on Microstructure and Mechanical Properties of Refractory CoCrMoNbTi0.4 High-Entropy Alloy. |
| المؤلفون: |
Zhang, Mina, Zhou, Xianglin, Zhu, Wuzhi, Li, Jinghao |
| المصدر: |
Metallurgical & Materials Transactions. Part A; Apr2018, Vol. 49 Issue 4, p1313-1327, 15p, 1 Color Photograph, 5 Black and White Photographs, 6 Charts, 5 Graphs |
| مصطلحات موضوعية: |
ANNEALING of metals, ALLOYS, VACUUM arcs, MICROSTRUCTURE, MICROHARDNESS, COMPRESSIVE strength, LAVES phases (Metallurgy) |
| مستخلص: |
A novel refractory CoCrMoNbTi0.4 high-entropy alloy (HEA) was prepared via vacuum arc melting. After annealing treatment at different temperatures, the microstructure evolution, phase stability, and mechanical properties of the alloy were investigated. The alloy was composed of two primary body-centered cubic structures (BCC1 and BCC2) and a small amount of (Co, Cr)2Nb-type Laves phase under different annealing conditions. The microhardness and compressive strength of the heat-treated alloy was significantly enhanced by the solid-solution strengthening of the BCC phase matrix and newborn Laves phase. Especially, the alloy annealed at 1473 K (1200 °C) achieved the maximum hardness and compressive strength values of 959 ± 2 HV0.5 and 1790 MPa, respectively, owing to the enhanced volume fraction of the dispersed Laves phase. In particular, the HEAs exhibited promising high-temperature mechanical performance, when heated to an elevated temperature of 1473 K (1200 °C), with a compressive fracture strength higher than 580 MPa without fracture at a strain of more than 20 pct. This study suggests that the present refractory HEAs have immense potential for engineering applications as a new class of high-temperature structural materials. [ABSTRACT FROM AUTHOR] |
|
Copyright of Metallurgical & Materials Transactions. Part A is the property of Springer Nature and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |
Find this article in full text from Springer Verlag. 
Full Text Finder