Change of the Phase Composition and Strength of Al2O3-ZrO2-Ceramic After Hydrothermal Aging. |
المؤلفون: |
Kuz’min, R. I., Veselov, S. V., Cherkasova, N. Yu., Stukacheva, N. S., Malyutina, Yu. N., Skiba, V. Yu. |
المصدر: |
Glass & Ceramics; Mar2018, Vol. 74 Issue 11/12, p415-419, 5p, 2 Charts, 3 Graphs |
مصطلحات موضوعية: |
CERAMIC materials, ALUMINUM oxide, ZIRCONIUM oxide, BIOCERAMICS, COMPOSITE materials |
مستخلص: |
The effect of Al2O3 weight content on the stability of the phase composition and strength of ceramic in the system Al2O3-3Y-ZrO2 prepared by a commercial technology was determined. It was shown that the introduction of aluminum oxide has a positive effect on the stability of the tetragonal phase of zirconium dioxide during accelerated aging. At the same time increasing the mass content of aluminum oxide from 15 to 80% does not significantly change the ratio t-ZrO2/m-ZrO2. It was observed that the strength of all materials containing aluminum oxide increases after aging for 5 h. [ABSTRACT FROM AUTHOR] |
|
Copyright of Glass & Ceramics is the property of Springer Nature and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
قاعدة البيانات: |
Complementary Index |