Enhancement of Mechanical Properties and Handling Characteristic of Tire Rubber Using Different Percentage of Nano Aluminum Oxide and Carbon Black. |
المؤلفون: |
Alkhazraji, Ahmed N. |
المصدر: |
International Journal of Nanoelectronics & Materials; 2018, Vol. 11 Issue 3, p263-270, 8p |
مصطلحات موضوعية: |
RUBBER testing, ALUMINUM oxide, CARBON-black, VULCANIZATION, STIFFNESS (Engineering) |
مستخلص: |
Rubber based composites are widely used especially in transportation. The goal of the this paper is to study mechanical properties and handling characteristics of rubber based composites of carbon black and Nano Alumina additive (50 nm), then select an optimal composition, then study the effect of adding particle on the cornering stiffness. Carbon black increased mechanical properties and enhanced the handling characteristics as well as Nano Alumina. The wear rate decreased rapidly with increasing nano filler percentage. Post UV (345 nm) laser vulcanization shows improvement in mechanical properties. The optimum values for composite rubber were (2.5% Nano Al2O3 and 60 phr Carbon Black) which gave 800%, decreasing in wear rate and slipping as well as an increasing about 22% in cornering stiffness of rubber composite, while slight increasing was carried out in hardness of the same composite rubber. [ABSTRACT FROM AUTHOR] |
|
Copyright of International Journal of Nanoelectronics & Materials is the property of Universiti Malaysia Perlis and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |