Problems of High-quality Doped Y2O3-ceramics Fabrication. |
| المؤلفون: |
Balashov, V. V., Kopylov, Yu. L., Kravchenko, V. B., Lopukhin, K. V., Ryabochkina, P. A., Chabushkin, A. N. |
| المصدر: |
KnE Engineering; 10/8/2018, p113-120, 8p |
| مصطلحات موضوعية: |
CERAMICS, FABRICATION (Manufacturing), METAL fabrication, SINTERING, OPTICAL quality control |
| مستخلص: |
Tm:Y2O3, Ho:Y2O3 and Yb:Y2O3 ceramic samples were fabricated using different heat treatments modes. La2O3 (0.5 mol.%) and ZrO2 (1.5 mol.%) were used as sintering additives. Based on the investigation of structural properties of obtained samples, annealing mode was adjusted, and another set of samples with better optical quality was fabricated. In-line transmittance of the latter samples is 70% at 400nm and 75.6% at 600nm. [ABSTRACT FROM AUTHOR] |
|
Copyright of KnE Engineering is the property of Knowledge E DMCC and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |