Physical and Mechanical Properties of Heat Affected Zone of Dissimilar Welds between Duplex Stainless Steel and Low Carbon Steel. |
المؤلفون: |
Dan, Nsikan Etim, Mahmud, Muhammad Shazwan, Hussain, Patthi, Mohebbi, Hamed, Kakooei, Saeid |
المصدر: |
AIP Conference Proceedings; 2018, Vol. 2035 Issue 1, p080007-1-080007-7, 7p |
مصطلحات موضوعية: |
DUPLEX stainless steel, CARBON steel, GAS tungsten arc welding, ARGON, OPTICAL microscopes |
مستخلص: |
Joining of duplex stainless steel (DSS) and low carbon steel (LCS) was performed using gas tungsten arc welding (GTAW) with aid of argon as a shielding gas. Sample was welded using ER308L weld wire to produce joined material. Physical and mechanical properties of the heat effect zone and the welded joint were investigated using optical microscope (OP), scanning electron microscope (SEM), Electron dispersive spectroscopy (EDS), hardness test and ultimate tensile test (UTS). SEM at the both sides of HAZ revealed difference in morphological changes at DSS HAZ and LCS HAZ with a precipitation of martensitic phase and chromium carbide respectively which are suspected to be responsible variation in mechanical properties at this region. UTS conducted also shows a plastic deformation mode of failure at the DSS HAZ while failure occurred at the HAZ of LCS indicating brittle property at this point. Redistribution and migration of manganese from DSS to LCS during welding from EDS is also suspected to be the reason for brittle property of HAZ of LCS [ABSTRACT FROM AUTHOR] |
|
Copyright of AIP Conference Proceedings is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
قاعدة البيانات: |
Complementary Index |