Characteristic the α Phase in Ti-6Al-6Mo Implant Alloy after Various Pre-Heating Time of Heavy Hot Rolling Process. |
| المؤلفون: |
Rokhmanto, Fendy, Nyoman Gede Putrayasa Astawa, I., Utomo, Edy Priyanto, Malau, Daniel Panghihutan, Purawiardi, Raden Ibrahim, Triwardono, Joko |
| المصدر: |
AIP Conference Proceedings; 2020, Vol. 2232 Issue 1, p070003-1-070003-6, 6p, 3 Diagrams, 1 Graph |
| مصطلحات موضوعية: |
HOT rolling, ALLOYS, BIOMATERIALS, HARDNESS testing, SCANNING electron microscopy, TUNGSTEN alloys, MICROSCOPY |
| مستخلص: |
Ti-based alloys are finding ever-increasing applications in biomaterials due to their excellent mechanical, physical and biological performance. Ti-6Al-6Mo shows good hot workability, mechanical behavior and corrosion-resistant. Therefore, this alloy has a potential used as a biomaterial implant. The effect of various pre-heating time and 88 % reduction of the hot rolling process was conducted to Ti-6Al-6Mo alloy. The study aim is to investigate the characteristic of α phase in Ti-6Al-6Mo alloy after pre-heating and heavy hot rolling. The homogenized Ti-6Al-6Mo alloy was preheated at 1000 ºC with a various holding time of 15, 30, and 60 min and followed by 88 % hot rolling. Microstructures of this alloy observed by optical microscopy (OM) and scanning electron microscopy (SEM). The hardness of Ti-6Al-6Mo alloy after the process was examined using Rockwell hardness testing machine scale C. The results showed the α phase characteristic was changed its morphology. The α phase leading to a globular structure and it’s increasing the hardness due to increasing pre-heating time. [ABSTRACT FROM AUTHOR] |
|
Copyright of AIP Conference Proceedings is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |