التفاصيل البيبلوغرافية
| العنوان: |
High performance, advanced-internal-magnesium-infiltration (AIMI) MgB2 wires processed using a vapor-solid reaction route. |
| المؤلفون: |
Wan, Fang, Sumption, Michael D, Rindfleisch, Matthew A, Thong, C J, Tomsic, Michael J, Collings, Edward W |
| المصدر: |
Superconductor Science & Technology; Sep2020, Vol. 33 Issue 9, p1-9, 9p |
| مصطلحات موضوعية: |
SUPERCONDUCTING wire, CRITICAL currents, WIRE, LOW temperatures |
| مستخلص: |
MgB2 superconducting wires made using a Mg infiltration method have reached a higher performance than either in-situ or ex-situ mixed powder based routes. Indeed, very high layer Jc coupled with whole-strand Je (critical current per total strand cross section) exceeding 104 A cm−2 at 4.2 K, 10 T have been found for monocore MgB2 wires. However, previous multicore infiltration route wires have not reached their potential for Je due to partially reacted and non-uniform MgB2 layers. This study shows that 18-core MgB2 AIMI wires processed using a low temperature route can attain higher and more uniform Je values due to a more uniform MgB2 reaction layer. The formation of fully reacted, uniform MgB2 layers is attributed to the switch from a liquid-solid to a vapor-solid reaction route. [ABSTRACT FROM AUTHOR] |
|
Copyright of Superconductor Science & Technology is the property of IOP Publishing and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |