3D-printable zwitterionic nano-composite hydrogel system for biomedical applications. |
المؤلفون: |
Sällström, Nathalie, Capel, Andrew, Lewis, Mark P, Engstrøm, Daniel S, Martin, Simon |
المصدر: |
Journal of Tissue Engineering; 10/29/2020, p1-11, 11p |
مصطلحات موضوعية: |
HYDROGELS, MECHANICAL ability, BETAINE, CELL culture, CELL survival, GEOMETRIC shapes, LEACHING |
مستخلص: |
Herein, the cytotoxicity of a novel zwitterionic sulfobetaine hydrogel system with a nano-clay crosslinker has been investigated. We demonstrate that careful selection of the composition of the system (monomer to Laponite content) allows the material to be formed into controlled shapes using an extrusion based additive manufacturing technique with the ability to tune the mechanical properties of the product. Moreover, the printed structures can support their own weight without requiring curing during printing which enables the use of a printing-then-curing approach. Cell culture experiments were conducted to evaluate the neural cytotoxicity of the developed hydrogel system. Cytotoxicity evaluations were conducted on three different conditions; a control condition, an indirect condition (where the culture medium used had been in contact with the hydrogel to investigate leaching) and a direct condition (cells growing directly on the hydrogel). The result showed no significant difference in cell viability between the different conditions and cells were also found to be growing on the hydrogel surface with extended neurites present. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Tissue Engineering is the property of Sage Publications Inc. and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
قاعدة البيانات: |
Complementary Index |