التفاصيل البيبلوغرافية
العنوان: |
Sn 量子点/石墨烯复合材料的合成及储锂性能. (Chinese) |
Alternate Title: |
Synthesis and lithium storage properties of Sn quantum dots/graphene composite. (English) |
المؤلفون: |
沈丁, 储诚议, 王来贵, 董伟, 刘耀汉, 李明月, 杨绍斌 |
المصدر: |
Acta Materiae Compositae Sinica; Mar2021, Vol. 38 Issue 3, p863-870, 8p |
مصطلحات موضوعية: |
COMPOSITE materials, GRAPHENE oxide, CHEMICAL reduction, CHEMICAL stability |
Abstract (English): |
The Sn-based materials have been a focus as promising high-capacity electrode materials of lithium-ion battery. However, its poor cycling performance has severely restricted the large-scale practical applications. The Sn quantum dot/graphene (SnQds/rGO) composite electrode material was synthesized by chemical reduction method, using graphene oxide as the carrier. The Sn quantum dots with < 10 nm were uniformly loaded on the surface of graphene. The experimental results show that the SnQds/rGO composite with Sn mass fraction of 90wt% has good comprehensive electrochemical performance. The first discharge capacity and Coulomb efficiency of the SnQds/rGO composite are 939 mAh/g and 66.6%, respectively. It’s discapacity can reach 621 mAh/g after 200 cycles and the capacity retention rate is 66.1%. The structure stability of SnQds/rGO composite is improve, meanwhile its impedance reduce, owing to the commposite of small size Sn quantum dots and graphenethe. As a result, the cycle performance and rate performance of the SnQds/rGO composite have been significantly improved. However, the initial Coulomb efficiency of SnQds/rGO composite decreases. [ABSTRACT FROM AUTHOR] |
Abstract (Chinese): |
Sn 基材料是目前高容量锂离子电池电极材料研究的热点,但循环性能较差阻碍了其大规模应用。以 氧化石墨烯为载体,通过化学还原法在载体表面成功均匀负载<10 nm 的 Sn 量子点,合成 Sn 量子点/石墨烯 (SnQds/rGO) 复合电极材料。结果表明,Sn 质量分数为 90wt% 的SnQds/rGO 复合材料具有良好的综合电化 学性能,首次放电容量和库伦效率分别为 939 mAh/g 和 66.6%,经过 200 次循环后容量可达 621 mAh/g,容 量保持率为 66.1%。小尺寸的 Sn 量子点与石墨烯复合能够增强电极材料的结构稳定性和降低阻抗,改善电极 材料的循环性能和倍率性能,但会导致首次库伦效率有所降低。 [ABSTRACT FROM AUTHOR] |
|
Copyright of Acta Materiae Compositae Sinica is the property of Acta Materiea Compositae Sinica Editorial Department and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |