Dense and core‐rim structured B4C‐TiB2 ceramics with Mo‐Co‐WC additive. |
| المؤلفون: |
Tan, Da‐Wang, Lao, Zhen‐Yong, Zhang, Zhan, Guo, Wei‐Ming, Sun, Shi‐Kuan, Lin, Hua‐Tay |
| المصدر: |
Journal of the American Ceramic Society; Jun2021, Vol. 104 Issue 6, p2860-2867, 8p, 1 Color Photograph, 3 Black and White Photographs, 1 Diagram, 1 Chart, 2 Graphs |
| مصطلحات موضوعية: |
VICKERS hardness, FRACTURE toughness, CERAMICS, SOLID solutions, ADDITIVES |
| مستخلص: |
B4C‐TiB2 ceramics (TiB2 ranging 5~70 vol%) with Mo‐Co‐WC as the sintering additive were prepared by spark plasma sintering. In comparison with B4C‐TiB2 without additive, the enhanced densification was evident in the sintered specimen with Mo‐Co‐WC additive. Core‐rim structured grain was observed around TiB2 grains. The interface of the rim between TiB2 and B4C phases demonstrated different feature: the inner borderline of the rim exhibited a smooth feature, whereas a sharp curved grain boundary was observed between the rim and the B4C grain. The formation mechanism is discussed: the epitaxial growth of (Ti,Mo,W)B2 rim around the TiB2 core may occur as a result of the solid solution and dissolution‐precipitation between TiB2 phase and the sintering additive. It was revealed that the fracture toughness increased as the content of TiB2 content increased, alongside the decreased hardness. B4C‐30 vol% TiB2 specimen demonstrated the optimal combination of mechanical properties, reaching Vickers hardness of 24.3 GPa and fracture toughness of 3.33 MPa·m1/2. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of the American Ceramic Society is the property of Wiley-Blackwell and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |
Full Text Finder