Luminescence and Conductivity of β-Ga2O3 and β-Ga2O3:Mg Single Crystals. |
| المؤلفون: |
VASYLTSIV, V., KOSTYK, L., TSVETKOVA, O., LYS, R., KUSHLYK, M., PAVLYK, B., LUCHECHKO, A. |
| المصدر: |
Acta Physica Polonica: A; Apr2022, Vol. 141 Issue 4, p312-318, 7p |
| مصطلحات موضوعية: |
SINGLE crystals, LUMINESCENCE, LUMINESCENCE quenching, FUSED silica, ACTIVATION energy, LOW temperatures |
| مستخلص: |
The temperature-dependencies of the X-ray excited luminescence spectra were measured from unintentionally doped, annealed in oxygen and Mg-doped β-Ga2O3 crystals prepared by the floating zone growth method. The crystals exhibited ultraviolet, blue and green luminescence bands. It was established that the luminescence intensity is strongly dependent on resistivity of the crystal. For the as-grown sample with a high electron concentration, the main luminescence band at 300 K was blue. The blue luminescence band was observed over a wide range of temperatures, and the thermal quenching of luminescence was observed only at T > 400 K. The blue luminescence band was suppressed in high-resistance crystals, in particular in oxygen annealed and heavily doped β-Ga2O3 crystals with 1% Mg, while the UV band, on the contrary, increased and prevailed at low temperatures. Activation energies of separate luminescence bands and conductivity in the investigated crystals are calculated. Some correlations between conductivity and luminescence parameters were found and discussed to give hints for the further development of this material. [ABSTRACT FROM AUTHOR] |
|
Copyright of Acta Physica Polonica: A is the property of Instytut Fizyki, Polska Akademia Nauk and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |