Study on the influence factors of silver powders size was prepared by liquid-phase reduction method. |
المؤلفون: |
Shi, Yu Meng, Zhao, Yu, Cao, Jia Feng, Jiang, Ke, Pan, Jun Li, Huang, Shou Qiang, Liu, Wei Qiao |
المصدر: |
Ferroelectrics; 2022, Vol. 596 Issue 1, p126-136, 11p |
مصطلحات موضوعية: |
POWDERS, SILVER, SILVER nitrate, SILVER nanoparticles, VITAMIN C |
مستخلص: |
Quasi-spherical silver was synthesized by reducing silver nitrate with ascorbic acid by the liquid-phase reduction method. The effects of the concentration of silver nitrate and ascorbic acid, feed rate, and pH on the particle size of the silver powder were studied. The best conditions for preparing silver powder by the orthogonal experiment are: silver nitrate concentration is 0.05 mol/L, feeding speed is 25 mL/min and pH = 6. The morphology of the silver powder prepared under the optimal conditions is spheroidal, uniformly dispersed, and the particle size is 1.81 μm. Silver nitrate concentration is the most influential in powders' size silver powder. [ABSTRACT FROM AUTHOR] |
|
Copyright of Ferroelectrics is the property of Taylor & Francis Ltd and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
قاعدة البيانات: |
Complementary Index |