Effect of therapeutic fractionated radiotherapy on bond strength and interfacial marginal adaptation of Adseal, MTA Fillapex, and EndoSequence BC sealer: An in vitro study. |
| المؤلفون: |
Khangwal, Monika, Solanki, Ravinder, Rahman, Hena |
| المصدر: |
Saudi Endodontic Journal; Sep-Dec2022, Vol. 12 Issue 3, p289-296, 8p |
| مستخلص: |
Introduction: The study aimed to assess the impact of fractionated radiation on push-out bond strength of sealer to dentin interface and on marginal adaptation of the sealer (Adseal, MTA Fillapex, and EndoSequence BC sealer) to irradiated dentin. Materials and Methods: Ninety maxillary central incisors were randomly divided into two groups: with irradiation (n = 45) and without (n = 45). All the samples to be radiated were exposed to fractionated dosage (60 Gy) through Co-60 gamma (1.17 and 1.33 Mev) photons. Specimens were prepared and subdivided into three subgroups (n = 15 each) according to assigned sealer Adseal, MTA Fillapex, and EndoSequence BC sealer. Later, the samples were sectioned into a 1 mm thick segment at each root third for bond strength and scanning electron microscope (SEM) analysis. SEM micrographs were analyzed with an ORION version 6 image analyzer. The percentage of failure mode after debonding was evaluated with a stereomicroscope. Bond strength data were analyzed using two-way analysis of variance and the Tukey's post hoc test. Results: Bond strength was significantly (P < 0.0001) decreased after radiotherapy (0.76 ± 0.12 Mpa) versus without radiation (0.93 ± 0.18 Mpa). Furthermore, when the pooled average of sealers was compared, significantly highest bond strength was perceived in Adseal (0.98 ± 0.18 Mpa) followed by EndoSequence BC (0.84 ± 0.13 Mpa). Coronal sections showed significantly (P < 0.0001) higher bond strength (0.99 ± 0.16 Mpa) compared to the middle (0.81 ± 0.14 MPa) and apical third (0.74 ± 0.12 Mpa). Qualitative SEM revealed a higher interfacial gap between sealer and irradiated radicular dentin. The percentage of mean change was recorded significantly high in MTA Fillapex (52%), then in EndoSequence BC (31%), and least was in Adseal (17%). Conclusions: Irradiated teeth resulted in consequential decreased adhesiveness and bond strength of dentin to root canal filling material. In addition, the highest bond strength was noticed in Adseal. [ABSTRACT FROM AUTHOR] |
|
Copyright of Saudi Endodontic Journal is the property of Wolters Kluwer India Pvt Ltd and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |
Full Text Finder