Lightweight Chain-Typed Magnetic Fe 3 O 4 @rGO Composites with Enhanced Microwave-Absorption Properties. |
المؤلفون: |
Qian, Congyi, Liang, Xiaohui, Wu, Mei, Zhang, Xingxin |
المصدر: |
Nanomaterials (2079-4991); Oct2022, Vol. 12 Issue 20, p3699-N.PAG, 13p |
مصطلحات موضوعية: |
ELECTROMAGNETIC wave absorption, IRON oxides, ELECTROMAGNETIC fields, ELECTROMAGNETIC compatibility, MAGNETIC materials, MAGNETIC fields |
مستخلص: |
A lightweight microwave-absorbing material with a strong electromagnetic-absorption capability of practical significance in the field of electromagnetic compatibility was obtained by adjusting the ratio of Fe3O4 and rGO. A nanoparticle material with a chain-typed structure consisting of a combination of Fe3O4 and rGO was produced by a hydrothermal method under an applied magnetic field. The electromagnetic loss property of the Fe3O4@rGO composites is studied in the frequency range from 2 to 18 GHz. In addition, the reflection loss and the mechanism of microwave absorption are explored. By changing the amounts of rGO, the electromagnetic loss of the Fe3O4@rGO composites can be effectively regulated, which obtain better reflection loss. The minimum reflection loss of the Fe3O4@rGO composites is −49.4 dB at 16.2 GHz only with a thickness of 1.75 mm. Thus, the Fe3O4@rGO composites have an extremely thin thickness and a strong electromagnetic wave absorption capacity, which is a candidate for the development of lightweight magnetic absorbing materials. [ABSTRACT FROM AUTHOR] |
|
Copyright of Nanomaterials (2079-4991) is the property of MDPI and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
قاعدة البيانات: |
Complementary Index |