Microstructure and Properties of Densified Gd 2 O 3 Bulk. |
| المؤلفون: |
Gao, Pei-Hu, Jin, Can, Zeng, Sheng-Cong, Xie, Rui-Guang, Zhang, Bo, Chen, Bai-Yang, Yang, Zhong, Guo, Yong-Chun, Liang, Min-Xian, Li, Jian-Ping, Zhang, Li-Na, Yan, Zhi-Yi, Jia, Lu, Zhao, Dan |
| المصدر: |
Materials (1996-1944); Nov2022, Vol. 15 Issue 21, p7793, 14p |
| مصطلحات موضوعية: |
MICROSTRUCTURE, ELASTIC modulus, FRACTURE toughness, THERMAL expansion, THERMAL conductivity, THERMAL barrier coatings |
| مستخلص: |
In this work, Gd2O3 bulks were sintered at temperatures ranging from 1400 °C to 1600 °C for times from 6 h to 24 h, and their microstructure and properties were studied for a wider application of materials in thermal barrier coatings. The densification of the Gd2O3 bulk reached 96.16% when it was sintered at 1600 °C for 24 h. The elastic modulus, hardness, fracture toughness and thermal conductivity of the bulks all increased with the rise in sintering temperature and extension of sintering time, while the coefficient of thermal expansion decreased. When the Gd2O3 bulk was sintered at 1600 °C for 24 h, it had the greatest elastic modulus, hardness, fracture toughness and thermal conductivity of 201.15 GPa, 9.13 GPa, 15.03 MPa·m0.5 and 2.75 W/(m·k) (at 1100 °C), respectively, as well as the smallest thermal expansion coefficients of 6.69 × 10−6/°C (at 1100 °C). [ABSTRACT FROM AUTHOR] |
|
Copyright of Materials (1996-1944) is the property of MDPI and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |
Full Text Finder