Investigation of near-room and high-temperature thermoelectric properties of (Bi0.98In0.02)2Se2.7Te0.3/Bi2Te3 composite system. |
| المؤلفون: |
Hegde, Ganesh Shridhar, Prabhu, A. N., Rao, Ashok, Gurukrishna, K., Deepika Shanubhogue, U. |
| المصدر: |
Journal of Materials Science: Materials in Electronics; Nov2022, Vol. 33 Issue 33, p25163-25173, 11p |
| مصطلحات موضوعية: |
THERMOELECTRIC materials, SEEBECK coefficient, FIELD emission, ELECTRICAL resistivity, SPACE groups, SELENIUM |
| مستخلص: |
Polycrystalline composite samples of (Bi0.98In0.02)2Se2.7Te0.3/Bi2Te3 with different concentrations of Bi2Te3 such as 5%,10%,15% and 20% were prepared by the solid-state reaction technique. The X-Ray diffraction analysis has shown the hexagonal composite crystal structure with space group of R 3 ¯ m. Field emission scanning electronic microscope shows secondary particles on the surface of the samples. All the samples have shown the usual semi-conducting behaviour throughout the temperature range. It is observed that bismuth has been co-ordinated with 6 selenium atoms in (Bi0.98In0,02)2Se2.7Te0.3 compound and it has enormous selenium vacancies. The electrical resistivity represents the noteworthy result of the grain boundaries leading to the higher content of scattering centres in the polycrystalline composite samples. It is found that the electronegativity differences of In and Te, In and Se are less than Bi and Se, Bi and Te is the reason for the decrease in Seebeck coefficient in the compound containing 15% and 20% of Bi2Te3. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Materials Science: Materials in Electronics is the property of Springer Nature and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |
Find this article in full text from Springer Verlag. 
Full Text Finder