Biologic Bone Behavior During the Osseointegration Process: Histologic, Histomorphometric, and SEM-EDX Evaluations. |
| المؤلفون: |
Mastrangelo, Filiberto, Parma-Benfenati, Stefano, Quaresima, Raimondo |
| المصدر: |
International Journal of Periodontics & Restorative Dentistry; Jan/Feb2023, Vol. 43 Issue 1, p65-72, 8p |
| مصطلحات موضوعية: |
BONE metabolism, BONES, BIOLOGICAL models, BONE density, OSSEOINTEGRATION, QUALITATIVE research, X-ray spectroscopy, ELECTRON probe microanalysis, TITANIUM, PHOSPHATES, BONE growth, BONE screws, TIBIA, QUANTITATIVE research, DESCRIPTIVE statistics, HISTOLOGICAL techniques, ANIMAL experimentation, SHEEP, SCANNING electron microscopy, COMPARATIVE studies |
| مستخلص: |
This study evaluated bone behavior during dynamic osseointegration. A total of 12 implants were placed in sheep tibia and analyzed at 15, 30, 60, and 90 days. Quantitative and qualitative bone behaviors were evaluated with histologic, histomorphometric, Alizarin Red S, and SEM-EDX (scanning electron microscopy with energy-dispersive x-ray spectroscopy) analysis. Twenty microanalyses were performed in chambers 1, 3, and 5 (a chamber is the distinctive space/bone volume between two coils of the implant screw) in distinctive zones: the titanium-bone interface (zone A), the middle chamber-bone front (zone B), the bone-surgical threading interface (zone C), and native bone (zone D; used as a control). The dynamic osseointegration index (DOI) and bone quality index (BQI) with calcium/phosphorus (Ca/P) content were detected to evaluate the osseointegration quality, bone-to-implant contact (BIC), and bone density around implants. At 15 days, initial bone formation with osteoid matrix deposition and different color intensities were observed (means: BIC = 23.3% ± 3.9%; DOI = 1.55). SEM-EDX analysis showed low mineralized bone/bone marrow with a very low Ca/P mean value. At 30 days, high new bone deposition with higher color intensity in the crestal portion was recorded (BIC = 77.3% ± 0.4%; DOI = 2.58). At 90 days, tight BIC to the middle and apical implant portions were detected, as well as several osteon structures in the crestal portion (BIC = 86.4% ± 0.6%; DOI = 0.96). During all observed time periods, the BQI showed 25% more Ca/P in zone A. Greater maturation degree and lower BQI were seen at zone A compared to the other zones. After 15 and 30 days, zones B and C (except for P in zone B) showed BQIs slightly over 50% and around 75%, respectively, confirming a progressively higher degree of bone maturation that proceeds with the osseointegration process. After 90 days, the BQI values of zones B and C (greater than 70% in zone B and around 90% in zone C) confirmed the bone mineralization and maturation process and an acceleration of implant osseointegration, while a lower BQI value (25%) was recorded in zone A. This study shows osseointegration as a variable dynamic process with a higher bone deposition in contact with the implant surface during the early phase, while in the active and later osseointegration times, the bone quality maturation showed higher values only "at distance" (growth of native bone to the implant surface, observed later in the osseointegration process). After 3 months (before loading), the BQI evaluation was lower (25%) in zone A, confirming that the healing and maturation process of the bone cannot be considered complete. [ABSTRACT FROM AUTHOR] |
|
Copyright of International Journal of Periodontics & Restorative Dentistry is the property of Quintessence Publishing Company Inc. and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |