التفاصيل البيبلوغرافية
| العنوان: |
Influence of Thickness of Opaque Porcelain and Alloy Color on the Final Color of Porcelain-Fused-to-Metal Restorations. |
| المؤلفون: |
Vichi, Alessandro, Corciolani, Gabriele, Carrabba, Michele, Munoz, Alvaro, Louca, Chris |
| المصدر: |
Materials (1996-1944); Jan2023, Vol. 16 Issue 1, p457, 9p |
| مصطلحات موضوعية: |
GOLD-platinum alloys, SCIENTIFIC literature, NICKEL-chromium alloys, DENTAL metallurgy, PORCELAIN, TWO-way analysis of variance, GOLD alloys, ALLOYS |
| مستخلص: |
Despite the advent of metal-free solutions, porcelain-fused-to-metal restorations (PFM) are still widely used. Particularly for the latest ceramic systems, scarce information is present in the scientific literature about the ideal opaque layer thickness and the alloy color impact to achieve the desired final color of PFM restorations. This study aimed to evaluate the influence of opaque thickness variation layered on different metal alloys on the final color of PFM restorations. Opaque porcelain of one metal–ceramic system (VITA VM13) was layered in four different thicknesses (0.10 mm, 0.15 mm, 0.20 mm, and 0.25 mm) on three differently colored dental alloys: a gold–platinum alloy (yellowish), a gold–palladium alloy (light grayish), and a nickel–chromium alloy (dark grayish). The veneering porcelain layered over the opaque was kept constant (Base Dentine 0.45 mm, Transpa Dentine 0.50 mm, and Enamel 0.20 mm). Sixty specimens were fabricated, five samples for each combination of alloy/opaque thickness. The color difference (ΔE) between specimen and reference was measured using a clinical spectrophotometer. The two-way ANOVA revealed that the thickness of both the opaque (p < 0.001) and the metal alloy (p < 0.001) significantly influenced the ΔE values. Gray-colored alloys covered by a 0.10 mm thick opaque layer enabled the closest color match, whereas this occurred for yellow-color alloys covered by a 0.15 mm thick opaque layer. In contrast, the samples covered by a 0.25 mm thick opaque layer obtained the worst ΔE. [ABSTRACT FROM AUTHOR] |
|
Copyright of Materials (1996-1944) is the property of MDPI and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |