Resin Cement/Enamel Interface: A Morphological Evaluation of the Acid-Base Resistant Zone, Enamel Etching Pattern, and Effect of Thermocycling on the Microshear Bond Strength. |
| المؤلفون: |
Kumagai, Rose Y., Tomohiro Takagaki, Takaaki Sato, Toru Nikaido, Giannini, Marcelo, Reis, Andre, Junji Tagami |
| المصدر: |
Journal of Adhesive Dentistry; 2023, Vol. 25 Issue 1, p71-78, 8p |
| مصطلحات موضوعية: |
BOND strengths, THERMOCYCLING, ENAMEL & enameling, CEMENT, ETCHING |
| مستخلص: |
Purpose: To evaluate the effects of etching mode (self-etch and etch-and-rinse) on acid-base resistant zone (ABRZ) formation at the resin cement/enamel interface and enamel etching pattern, as well as the effects of thermocycling (0, 5000, and 10,000 cycles) on the enamel microshear bond strength (μSBS) mediated by dual-cure resin cements (DCRC). Materials and Methods: Two DCRC were used in 4 groups: Panavia V5 in self-etch (V5NE) and etch-and-rinse mode (V5E); and Estecem II in self-etch (ENE) and etch-and-rinse mode (EE). For ABRZ observation, the bonded interface was subjected to a demineralizing solution. The morphological attributes of the interface and etching patterns were observed using FE-SEM. For μ-SBS, cylinders with a 0.79-mm internal diameter and 0.5-mm height were made with DCRC and tested in shear after 0, 5000, and 10,000 thermal cycles (TC) (5°C and 55°C) (n = 10). Results: The formation of an enamel ABRZ was observed in all groups with different morphological features between self-etch and etch-and-rinse groups. A funnel-shaped erosion beneath the interface was present using V5NE and ENE modes where enamel was dissolved, while ABRZ formation was confirmed and no funnel-shaped erosion was noticed using V5E and EE. No significant differences in μSBS were observed between resin cements. However, significantly lower µSBSs were recorded when the self-etching mode was used. Thermocycling resulted in a significant reduction in µSBS for all groups. Conclusion: Selective enamel etching should be recommended to improve the interfacial quality when dual-cure resin luting cements are used. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Adhesive Dentistry is the property of Quintessence Publishing Company Inc. and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |
Full Text Finder