التفاصيل البيبلوغرافية
| العنوان: |
(In,Ga)As sidewall quantum wires on shallow-patterned InP (311)A. |
| المؤلفون: |
Zhou, D., Nötzel, R., Gong, Q., Offermans, P., Koenraad, P. M., van Veldhoven, P. J., van Otten, F. W. M., Eijkemans, T. J., Wolter, J. H. |
| المصدر: |
Journal of Applied Physics; 3/15/2005, Vol. 97 Issue 6, p063510, 5p, 1 Color Photograph, 6 Graphs |
| مصطلحات موضوعية: |
NANOWIRES, QUANTUM wells, TEMPERATURE, CRYSTAL growth, SPECTRUM analysis, MOLECULAR beam epitaxy |
| مستخلص: |
(In,Ga)As sidewall quantum wires (QWires) are realized by chemical beam epitaxy along [01-1] mesa stripes on shallow-patterned InP (311)A substrates. The QWires exhibit strong lateral carrier confinement due to larger thickness and In composition compared to the adjacent quantum wells, as determined by cross-sectional scanning-tunneling microscopy and microphotoluminescence (micro-PL) spectroscopy. The PL of the (In,Ga)As QWires with InP and quaternary (Ga,In)(As,P) barriers reveals narrow linewidth, high efficiency, and large lateral carrier confinement energies of 60–70 meV. The QWires are stacked in growth direction with identical PL peak emission energy. The PL emission energy is not only controlled by the (In,Ga)As layer thickness but also by the patterned mesa height. Stacked (In,Ga)As QWires with quaternary barriers exhibit room temperature PL emission at 1.55 μm in the technologically important wavelength region for telecommunication applications. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Applied Physics is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |
Find this article in full text from Scitation.