Interphase optimization of SiCf/Si3N4 composites. (English) |
| المؤلفون: |
DENG Yangfang, CHEN Xu, WANG Tongtong, FAN Xiaomeng |
| المصدر: |
Journal of Aeronautical Materials; 2023, Vol. 43 Issue 3, p72-78, 7p |
| مصطلحات موضوعية: |
FIBROUS composites, TRANSMISSION electron microscopes, SCANNING electron microscopes, FINITE element method, FRACTURE toughness, RESIDUAL stresses |
| مستخلص: |
SiC fiber reinforced Si3N4 composites (SiCf/Si3N4) were prepared by chemical vapor infiltration, and the mechanical properties were optimized by tailoring the BN interphase thickness. The microstructure was characterized by transmission electron microscope and scanning electron microscope, and the evolution of mechanical properties was revealed by the finite element analysis. The results show that with the increase of BN interphase thickness from 290 to 550 nm, the flexural strength is increased from (190±39) MPa to ( 317±28) MPa, the fracture toughness is increased from (7.3±1.6) MPa•m1/2 to (14.7±0.5) MPa•m1/2, and the tensile strength is increased from (89±3) MPa to (176±17) MPa. The residual stress of the fiber decreases rapidly with the increase of BN interphase thickness, and the thermal mismatch is effectively alleviated, which makes the material show better mechanical properties. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Aeronautical Materials is the property of Editorial Board of Journal of Aeronautical Materials and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |
Full Text Finder