التفاصيل البيبلوغرافية
| العنوان: |
The Influence of Strain on Texture Changes and Phase Transformations in the Quenched Ti92.5Nb5Mo2.5 Alloy. |
| المؤلفون: |
Myslyvchenko, O. M., Podrezov, Yu. M., Bondar, A. A., Verbylo, D. G., Nazarenko, V. A., Voblikov, V. M. |
| المصدر: |
Powder Metallurgy & Metal Ceramics; Mar2023, Vol. 61 Issue 11/12, p748-753, 6p |
| مصطلحات موضوعية: |
PHASE transitions, ALLOY texture, MARTENSITIC transformations, YOUNG'S modulus, STRAIN gages, TITANIUM alloys |
| مستخلص: |
The strain-induced martensitic transformation in a medical alloy from the ternary Ti–Nb–Mo system was studied. The low-doped Ti92.5Nb5Mo2.5 alloy was produced by arc remelting, followed by annealing, rolling at room temperature, reannealing, and water quenching. X-ray diffraction analysis showed that thermomechanical processing resulted in the alloy primarily consisting of orthorhombic martensite (αʺ) with a small amount of the β-titanium phase. Hysteresis loops were recorded in loading–unloading cycles with 1% strain increments up to a total strain of 4% under compression testing, employing a precision strain gauge. Young's modulus under loading varied from 51.2 GPa at the initial section to 39.7 GPa after a 2% residual strain. Young's modulus remains unchanged, within 74.3 GPa, during unloading. Elastic, pseudoelastic, and plastic strains were found to significantly depend on the previous strain within the first three loading–unloading cycles. To examine the impact of higher strains (up to 23.4%) on structural rearrangements and phase transformations, the samples were compressed without a precision strain gauge. X-ray diffraction analysis revealed that only the crystalline texture of the alloy changed after compression. Strains exceeding 23.4% were achieved by rolling at room temperature. After rolling to a strain of 64%, the diffraction patterns indicated an increased amount of the β-phase, as evidenced by the (200) diffraction peak, not observed previously. The increased amount of the β-phase suggests that strain prompted the reverse martensitic transformation (αʺ → β). [ABSTRACT FROM AUTHOR] |
|
Copyright of Powder Metallurgy & Metal Ceramics is the property of Springer Nature and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |
Find this article in full text from Springer Verlag. 
Full Text Finder