Electron affinity of metal oxide thin films of TiO2, ZnO, and NiO and their applicability in 28.3 THz rectenna devices. |
| المؤلفون: |
Tekin, S. B., Almalki, S., Finch, H., Vezzoli, A., O'Brien, L., Dhanak, V. R., Hall, S., Mitrovic, I. Z. |
| المصدر: |
Journal of Applied Physics; 8/28/2023, Vol. 134 Issue 8, p1-13, 13p |
| مصطلحات موضوعية: |
ELECTRON affinity, ZINC oxide films, OXIDE coating, THIN films, METALLIC oxides, X-ray photoelectron spectroscopy |
| مستخلص: |
The holy grail of achieving efficient operation of infrared (IR) rectennas continues to be the realization of a high performance rectifier. In this paper, we have fabricated metal–insulator–metal (MIM) diodes based on TiO2, ZnO, and NiO thin films using shadow mask evaporation, photolithography, and sputtering. The electron affinities of oxides have been measured by a combination of variable angle spectroscopic ellipsometry and x-ray photoelectron spectroscopy, as well as deduction from the extraction of metal/oxide barrier heights of Fowler–Nordheim tunneling plots. Our results confirm a low value for the electron affinity of NiOx of ∼2.1–2.5 eV, which correlates with the high zero-bias dynamic resistance (RD0) of ∼500 kΩ of an associated MIM diode. These values render NiOx to be unsuitable for use in a rectenna device. Better performance has been observed from diodes based on TiO2 and ZnOx films. The best rectification performance was achieved for a Au/2.6 nm ZnOx/Cr diode, scaled down to 1 μm2 device area, showing a zero-bias dynamic resistance of RD0 = 71 kΩ, zero-bias responsivity β0 = 0.28 A/W, and a coupling efficiency of ηc = 2.4 × 10−5% for rectification at 28.3 THz. The main significance of this study is that it employs a methodology whereby key parameters of the MIM stack are derived from physical measurements, which are then used to assist in the fitting of electrical current–voltage data to produce a reliable appraisal of diode performance in an IR rectenna. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Applied Physics is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |