التفاصيل البيبلوغرافية
| العنوان: |
Capacitive and Resistive Properties of Molten Salt Synthesized Lead-Free K1/2Na1/2NbO3 Ceramic. |
| المؤلفون: |
Chakram, Deva Sucharitha, Reddy, Varimalla Raghavendra, Kumar, S. Nabanita, Dasari, Madhavaprasad |
| المصدر: |
Journal of Inorganic & Organometallic Polymers & Materials; Sep2023, Vol. 33 Issue 9, p2824-2834, 11p |
| مصطلحات موضوعية: |
LEAD-free ceramics, FUSED salts, SCANNING electron microscopy, LOW temperatures, SURFACE morphology, IMPEDANCE spectroscopy |
| مستخلص: |
Lead-free K1/2Na1/2NbO3 (KNN) powder was synthesized using the molten-salt process in the eutectic mixture of KCl–NaCl at a low temperature of 700 ℃ for 2 h, which is less than that of the widely used conventional technique solid-state synthesis. X-ray diffraction (XRD) was used to investigate the purity and phase formation. To characterize the surface morphology of sintered ceramics, scanning electron microscopy (SEM) is used. The studies of dielectric permittivity and impedance spectroscopy were performed ranging from 1 Hz to 1 MHz on KNN at temperatures ranging from room temperature (RT) to 580 ℃. The piezoelectric coefficient constant d33 of KNN was obtained, and it is 90 × 10−12 pC/N. Nyquist plots of complex impedance were used to deduce the mechanism of relaxation. These plots depict non-Debye relaxation behavior. The conductivity contributions of grain and grain boundary were estimated using Cole–Cole plots. In addition, antibacterial activity for the KNN was tested using a four-plate approach. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Inorganic & Organometallic Polymers & Materials is the property of Springer Nature and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |