Effect of Casting Speed on Floating Grains in Direct-Chill Casting of Aluminum Alloys. |
| المؤلفون: |
Yi Zhang, Jianquan Ling, Ziwei Yao, Fangzhen Liu, Qipeng Dong, Hiromi Nagaumi |
| المصدر: |
Materials Transactions; 2023, Vol. 64 Issue 9, p2309-2314, 6p |
| مصطلحات موضوعية: |
ALUMINUM alloys, ALUMINUM castings, SPEED, GRAIN |
| مستخلص: |
The effects of casting speed on macrosegregation and grain structure during the direct-chill casting of an Al–Mg–Si alloy are experimentally investigated. Results show that increasing the casting speed yields a more pronounced negative centerline segregation. Regard this mechanism, apart from the increased contribution of solidification shrinkage, the variation in floating grains is newly observed. The increased casting speed significantly increases the size and fraction of floating grains at the central portion of the billet, thus resulting in a more severe negative segregation. To clarify the experimentally observed phenomena, the solidification and distribution of floating grains in billets cast at different casting speeds are numerically simulated. The increased casting speed deepens the slurry zone significantly, thus providing more time for the floating grains to freely float and develop before settling into the mushy zone. Additionally, the greater slope of the coherency isotherm resulting from the increased casting speed promotes the movement and sedimentation of the floating grains toward the central portion of the billet. Consequently, more floating grains are detected at the billet center. [ABSTRACT FROM AUTHOR] |
|
Copyright of Materials Transactions is the property of Japan Institute of Metals & Materials and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |